SABIC Innovative Plastics LNP STAT-KON Noryl_NC3508 PPE+HIPS (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON Noryl_NC3508 PPE+HIPS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PRELIMINARY DATA. LNP* Stat-kon* Noryl_NC3508 compound is a 33% glass/mineral/carbon filled PPE+PS. ESD, high heat, tight tolerance: electronic packaging/chip trays.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.00080 - 0.0018 cm/cm @Thickness 3.20 mm |
0.00080 - 0.0018 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.00090 - 0.0019 cm/cm @Thickness 3.20 mm |
0.00090 - 0.0019 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 119 MPa | 17300 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 117 MPa | 17000 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 4.5 % | 4.5 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 1.5 % | 1.5 % | Type I, 5 mm/min; ASTM D638 |
| Flexural Modulus | 9.65 GPa | 1400 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 9.74 GPa | 1410 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.420 J/cm | 0.787 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.24 J/cm | 4.20 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 179 °C @Thickness 3.20 mm |
354 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C @Thickness 3.20 mm |
351 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 50000 ohm-cm | 50000 ohm-cm | ASTM D257 |
| Surface Resistance | 1e+05 | 1e+05 | ASTM D257 |
| Static Decay | 0.010 sec | 0.010 sec | 5000V to <50V; FTMS101B |
Users viewing this material also viewed the following:
- Mid-Mountain Materials THERMOSEAL® FIBERPAK® M33 Moldable
- SABIC Innovative Plastics ULTEM PW2100 PEI (Europe-Africa-Middle East)
- Stir SpA AF 95 (PVC)
- Hexcel® Fibrelam® Grade 1-4/2 Panels for Aircraft Flooring
- Chosun Refractories TAST-170 Monolithic Refractories for Ladle and Tundish
- Arlon LW401R##-P0 0.040" (1.02 mm) Cured Self-Fusing Silicone Tape (Triangular, Unsupported)
- Solvay Specialty Polymers Algoflon® L100 Polytetrafluoroethylene (PTFE) (Unverified Data**)
- DuPont Performance Polymers Neoprene SW Polychloroprene Rubber (discontinued **)
Copyright © lookpolymers.com All Rights Reserved