SABIC Innovative Plastics LNP STAT-KON MD000ISC PP (Asia Pacific)
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON MD000ISC PP (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* MD000ISC is a compound based on Polypropylene resin containing Carbon Powder. Added features of this material include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.980 g/cc | 0.0354 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0300 % | 0.0300 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.016 - 0.018 cm/cm @Time 86400 sec |
0.016 - 0.018 in/in @Time 24.0 hour |
ASTM D955 |
| 0.016 - 0.018 cm/cm @Time 86400 sec |
0.016 - 0.018 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0158 - 0.018 cm/cm @Time 86400 sec |
0.0158 - 0.018 in/in @Time 24.0 hour |
ISO 294 |
| 0.016 - 0.018 cm/cm @Time 86400 sec |
0.016 - 0.018 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 17.0 MPa | 2470 psi | ASTM D638 |
| 17.0 MPa | 2470 psi | ISO 527 | |
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | ISO 527 |
| 21.0 MPa | 3050 psi | ASTM D638 | |
| Elongation at Break | 133.8 % | 133.8 % | ASTM D638 |
| Elongation at Yield | 9.0 % | 9.0 % | ASTM D638 |
| Tensile Modulus | 0.480 GPa | 69.6 ksi | 50 mm/min; ASTM D638 |
| 1.10 GPa | 160 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 27.0 MPa | 3920 psi | ASTM D790 |
| 27.0 MPa | 3920 psi | ISO 178 | |
| Flexural Modulus | 1.13 GPa | 164 ksi | ASTM D790 |
| 1.20 GPa | 174 ksi | ISO 178 | |
| Izod Impact, Notched | 8.33 J/cm | 15.6 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 15.53 J/cm | 29.09 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 65.0 kJ/m² | 30.9 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 112 kJ/m² | 53.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 24.0 J | 17.7 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 81.0 °C @Thickness 3.20 mm |
178 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 52.0 °C @Thickness 3.20 mm |
126 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10 - 1.00e+6 ohm | 10 - 1.00e+6 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Parker Chomerics Tecknit Teckfip™ HC FIP-C Formed in Place Conductive Elastomer
- SABIC Innovative Plastics LNP LUBRICOMP DP003EH PC (Asia Pacific)
- Spartech Royalstatâ„¢ R63 ABS/PVC Static Control Sheet
- Techmer ES Elastoblend® PA6/6 IM1 L 33% Glass Filled
- Plastics Group Polifil® GFABS-20 20% Glass-Reinforced Acrylonitrile-Butadiene Styrene (ABS)
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 45 PHR Iceberg Clay Filler
- CMW® ELKONITE 4050 tungsten, high silver
- BASF Ultradur® S 4090 GM13 5/15% Glass/Mineral Filled PBT
- SABIC Innovative Plastics PC1800R PC (Europe-Africa-Middle East)
- ITW Plexus Plexus™ MA925 Methacrylate Adhesive
Copyright © lookpolymers.com All Rights Reserved