SABIC Innovative Plastics LNP STAT-KON MD000 PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON MD000 PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* MD000 is a compound based on Polypropylene resin containing Carbon Powder. Added feature of this material is: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in³ | ASTM D792 |
| 0.950 g/cc | 0.0343 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.0300 % | 0.0300 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0300 % | 0.0300 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.013 - 0.016 cm/cm @Time 86400 sec |
0.013 - 0.016 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0152 cm/cm @Time 86400 sec |
0.0152 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0133 cm/cm @Time 86400 sec |
0.0133 in/in @Time 24.0 hour |
ISO 294 |
| 0.013 - 0.016 cm/cm @Time 86400 sec |
0.013 - 0.016 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 15.0 MPa | 2180 psi | ISO 527 |
| 16.0 MPa | 2320 psi | ASTM D638 | |
| Tensile Strength, Yield | 21.0 MPa | 3050 psi | ASTM D638 |
| 21.0 MPa | 3050 psi | ISO 527 | |
| Elongation at Break | 47.6 % | 47.6 % | ASTM D638 |
| 52 % | 52 % | ISO 527 | |
| Elongation at Yield | 6.2 % | 6.2 % | ISO 527 |
| 8.4 % | 8.4 % | ASTM D638 | |
| Tensile Modulus | 1.22 GPa | 177 ksi | 1 mm/min; ISO 527 |
| 1.25 GPa | 181 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 24.0 MPa | 3480 psi | ISO 178 |
| 29.0 MPa | 4210 psi | ASTM D790 | |
| Flexural Modulus | 1.16 GPa | 168 ksi | ISO 178 |
| 1.17 GPa | 170 ksi | ASTM D790 | |
| Izod Impact, Notched | 8.17 J/cm | 15.3 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| Izod Impact, Notched (ISO) | 60.0 kJ/m² | 28.6 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 33.0 J | 24.3 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 32.0 J | 23.6 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 102 µm/m-°C @Temperature -40.0 - 40.0 °C |
56.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 102 µm/m-°C @Temperature -40.0 - 40.0 °C |
56.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 105 µm/m-°C @Temperature -40.0 - 40.0 °C |
58.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 105 µm/m-°C @Temperature -40.0 - 40.0 °C |
58.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 53.0 °C | 127 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 51.0 °C @Thickness 3.20 mm |
124 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 1.00e+6 ohm | 100 - 1.00e+6 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Potters Industries Conduct-O-Fil® SN325P25-LD Silver-coated Nickel Granules
- Polymer Resources PC-UV4 Polycarbonate, UV-stabilized, Easy Flow
- Formosa Plastics Formolene® LH5326 Injection Molding HDPE (discontinued **)
- SABIC Innovative Plastics PC0703 PC (Asia Pacific)
- SABIC Innovative Plastics ULTEM 2410R PEI
- SABIC Innovative Plastics NORYL PN235 PPE+PS
- Wingate Alloys Winco Poly NLT Engineered UHMW
- Dow Corning 203 Fluid
- Solvay Specialty Polymers Solef® 11008 PVDF Copolymer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved