SABIC Innovative Plastics LNP STAT-KON EX03319C PEI (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON EX03319C PEI (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-Kon* EX03319C is a polyetherimide compound reinforced with carbon fiber for good stiffness, dimension stability and has extremely high level of cleanliness for the most demanding application. A unique feature of this material is its low non-volatile residue (NVR). This compound is manufactured using LNP CCS Technology.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.351 g/cc | 0.04881 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.200 % | 0.200 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.00050 - 0.0015 cm/cm @Time 86400 sec |
0.00050 - 0.0015 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0045 cm/cm @Time 86400 sec |
0.0030 - 0.0045 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 224 MPa | 32500 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 2.3 % | 2.3 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 16.96 GPa | 2460 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 233 MPa | 33800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 11.6 GPa | 1680 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.54 J/cm | 6.63 ft-lb/in | ASTM D4812 |
| Charpy Impact Unnotched | 2.20 J/cm² | 10.5 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C @Thickness 3.20 mm |
401 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 5000 - 5.00e+6 ohm-cm | 5000 - 5.00e+6 ohm-cm | ASTM D257 |
| Surface Resistance | 5000 - 500000 ohm | 5000 - 500000 ohm | ASTM D257 |
| Static Decay | 0.10 sec | 0.10 sec | 5000V to <50V; FTMS101B |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® FXD121R PC (Europe-Africa-Middle East)
- KB Alloys 20% Calcium Aluminum Alloy
- Gromax PBT 1100-211M
- Multibase Multi-Flex® A 6221 E Black TPE Thermoplastic Elastomer
- Star Plastics PC1510FR Molding Grade PC
- Solvay Specialty Polymers Ryton® R-4-220NA Polyphenylene Sulfide (PPS), 40% Glass Fiber
- SABIC Innovative Plastics LNP THERMOCOMP RC008ESS PA 66 (Europe-Africa-Middle East)
- EMS-Grivory Grivory® TR 90 NZZ nat PAMACM12-I
- DuPont Teijin Films Mylar® 850H Polyester Film, 80 Gauge
- CENTROPLAST CENTROMID 6 GF 30 Polyamide 6 30% glass fiber
Copyright © lookpolymers.com All Rights Reserved