ATI Allegheny Ludlum 440A Martensitic Stainless Steel

Category	Metal , Ferrous Metal , Martensitic , Stainless Steel , T 400 Series Stainless Steel
Manufacturer	ATI Allegheny Ludlum
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ATI Allegheny Ludlum 440A Martensitic Stainless Steel.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Characteristics: superior wear resistance, hardenable, excellent corrosion resistance. Applications:cutlery, dental and surgical instruments, nozzles, valve parts, hardened steel ball and seats for oil well pumps, separating screens and strainers, springs, shears, and wear surfaces. Information provided by Allegheny Ludlum

Physical Properties	Metric	English	Comments
Density	7.72 g/cc	0.279 lb/in³

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell B	95	95
Hardness, Rockwell C	31	31	Hardened+Tempered 1200°F
	41	41	Hardened+Tempered 1000°F
	50	50	Hardened+Tempered 550°F
	52	52	Hardened+Tempered 900°F
	53	53	Hardened+Tempered 600°F
	53	53	Hardened+Tempered 800°F
	54	54	Hardened+Tempered 400°F
Tensile Strength, Ultimate	717 MPa	104000 psi	Annealed
	933 MPa	135000 psi	Hardened 1900°F, Tempered 1200°F
	1224 MPa	177500 psi	Hardened 1900°F, Tempered 1000°F
	1858 MPa	269500 psi	Hardened 1900°F, Tempered 900°F
	1879 MPa	272500 psi	Hardened 1900°F, Tempered 550°F
	1881 MPa	272800 psi	Hardened 1900°F, Tempered 800°F
	1883 MPa	273100 psi	Hardened 1900°F, Tempered 600°F
	2022 MPa	293300 psi	Hardened 1900°F, Tempered 400°F
Tensile Strength, Yield	727 MPa	105000 psi	Hardened 1900°F, Tempered 1200°F
	1013 MPa	146900 psi	Hardened 1900°F, Tempered 1000°F
	1466 MPa	212600 psi	Hardened 1900°F, Tempered 900°F
	1518 MPa	220200 psi	Hardened 1900°F, Tempered 550°F
	1531 MPa	222100 psi	Hardened 1900°F, Tempered 600°F
	1579 MPa	229000 psi	Hardened 1900°F, Tempered 400°F
	1610 MPa	234000 psi	Hardened 1900°F, Tempered 800°F
	427 MPa @Strain 0.200 %	61900 psi @Strain 0.200 %	Annealed
Elongation at Break	20 %	20 %	Annealed

Thermal Properties	Metric	English
CTE, linear	15.0 µm/m-°C @Temperature 20.0 - 200 °C	8.33 µin/in-°F @Temperature 68.0 - 392 °F
	16.8 µm/m-°C @Temperature 20.0 - 600 °C	9.33 µin/in-°F @Temperature 68.0 - 1110 °F
Specific Heat Capacity	0.460 J/g-°C	0.110 BTU/lb-°F
Thermal Conductivity	24.2 W/m-K @Temperature 100 °C	168 BTU-in/hr-ft²-°F @Temperature 212 °F
Melting Point	1399 - 1510 °C	2550 - 2750 °F
Solidus	1399 °C	2550 °F
Liquidus	1510 °C	2750 °F

Component Elements Properties	Metric	English	Comments
Carbon, C	0.60 - 0.75 %	0.60 - 0.75 %
Chromium, Cr	16 - 18 %	16 - 18 %
Iron, Fe	77.9 - 83.4 %	77.9 - 83.4 %	as balance
Manganese, Mn	<= 1.0 %	<= 1.0 %
Molybdenum, Mo	<= 0.75 %	<= 0.75 %
Nickel, Ni	<= 0.50 %	<= 0.50 %
Phosphorous, P	<= 0.040 %	<= 0.040 %
Silicon, Si	<= 1.0 %	<= 1.0 %
Sulfur, S	<= 0.030 %	<= 0.030 %

Electrical Properties	Metric	English	Comments
Electrical Resistivity	0.0000620 ohm-cm	0.0000620 ohm-cm

Descriptive Properties	Value	Comments
Corrosion Rate mils per year	0.35 (5% Phosphoric Acid at 49°C)	Hardened martensitic grades were tested after tempering at 204°C
	2.31 (5% Acetic Acid at 49°C)	Hardened martensitic grades were tested after tempering at 204°C
Pitting Potential, Volts vs. Sat. Calomel Electrode	0.598	100 ppm Chloride solution at 24°C, pH5. Samples had ground surface. Hardened martensitic grades were tested after tempering at 204°C.

Users viewing this material also viewed the following: