- HOME
- POLYMER SEARCH
- Thermoplastic
- Ethylene Vinyl Acetate
- Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
- LG Chemical SEETEC EF321 Ethylene Vinyl Acetate
LG Chemical SEETEC EF321 Ethylene Vinyl Acetate
| Category | Polymer , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade |
| Manufacturer | LG Chemical |
| Trade Name | SEETEC |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical SEETEC EF321 Ethylene Vinyl Acetate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics: Good Mechanical Properties. Good Optical Properties. Additives : No Additive Applications: Agricultural FilmCSA No. 25895-47-0Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.928 - 0.932 g/cc | 0.928 - 0.932 g/cc | ASTM D1505 |
| Melt Flow | 0.80 - 1.2 g/10 min @Load 2.61 kg, Temperature 190 °C |
0.80 - 1.2 g/10 min @Load 5.75 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 19.6 MPa | 2840 psi | 500mm/min; ASTM D638 |
| Film Elongation at Break, MD | 400 % | 400 % | 500 mm/min; ASTM D638 |
| Film Elongation at Break, TD | 650 % | 650 % | 500 mm/min; ASTM D638 |
| Elongation at Break | 650 % | 650 % | 500 mm/min; ASTM D638 |
| 2% Secant Modulus | 0.650 GPa | 94.3 ksi | 500mm/min; ASTM D638 |
| Elmendorf Tear Strength MD | 220 g | 220 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 260 g | 260 g | ASTM D1922 |
| Dart Drop Test | >= 400 g | >= 0.882 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 30.4 MPa | 4410 psi | 500mm/min, Ultimate; ASTM D638 |
| Film Tensile Strength at Break, TD | 30.4 MPa | 4410 psi | 500mm/min, Ultimate; ASTM D638 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 94.0 °C | 201 °F | 10°C/min; ASTM D3418 |
| Vicat Softening Point | 85.0 °C | 185 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 3.5 % | 3.5 % | ASTM D1003 |
| Gloss | 105 % | 105 % | 45°; ASTM D2457 |
Users viewing this material also viewed the following:
- Polykemi AB POLYelast TPE Z800 Thermoplastic Elastomer, SEBS-based
- Plastcom SLOVAMID 6 GB 30 TS PA6, 30% glass beads
- Ineos ABS Lustran® Guardian™ 620 ABS, Extrusion Grade
- ExxonMobil 1500 Mobilgear SHC Series
- Fainplast Compounds PH 75/SN Flexible PVC, Transparent Extrusion
- Azoty Tarnow™ Tarnamid® T-27 GF30 I Polyamide 6 - Glass Fiber Reinforced
- 3M FV039 Indoor UL Recognized White Vinyl Label Products
- Atom Adhesives AA-BOND F110 Epoxy Adhesive
- Teknor Apex Elexar® EL 3954-80 Thermoplastic Elastomer
- Beijing Evergrow Resources PB-30 Glass Fiber Tissue
Copyright © lookpolymers.com All Rights Reserved