SABIC Innovative Plastics LNP STAT-KON DEL22P PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DEL22P PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* DEL22P is a compound based on Polycarbonate resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D792 |
| 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| 0.180 % | 0.180 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | SABIC Method |
| 0.0010 - 0.0030 cm/cm @Thickness 0.750 - 2.30 mm |
0.0010 - 0.0030 in/in @Thickness 0.0295 - 0.0906 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | SABIC Method |
| 0.0040 - 0.0060 cm/cm @Thickness 0.750 - 2.30 mm |
0.0040 - 0.0060 in/in @Thickness 0.0295 - 0.0906 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 100 MPa | 14500 psi | ASTM D638 |
| 101 MPa | 14600 psi | ISO 527 | |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| 2.0 % | 2.0 % | ISO 527 | |
| Tensile Modulus | 7.90 GPa | 1150 ksi | 50 mm/min; ASTM D638 |
| 8.17 GPa | 1180 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 152 MPa | 22000 psi | ASTM D790 |
| Flexural Modulus | 0.150 GPa | 21.8 ksi | ISO 178 |
| 5.69 GPa | 825 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.740 J/cm | 1.39 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.83 J/cm | 5.30 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 34.0 kJ/m² | 16.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 13.0 J | 9.59 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 102 J | 75.2 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.55 | 0.55 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.52 | 0.52 | ASTM D3702 Modified |
| K (wear) Factor | 30.2 x 10-8 mm³/N-M | 15.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 14.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
7.78 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 15.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
8.33 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 76.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
42.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 76.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
42.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 143 °C | 289 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 134 °C @Thickness 3.20 mm |
273 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 100 ohm-cm | 100 ohm-cm | IEC 60093 |
| Surface Resistance | 100 - 1.00e+6 ohm | 100 - 1.00e+6 ohm | ROA; IEC 60093 |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 0112 Black Polypropylene
- Parker Chomerics CHO-BOND 1086 Conductive Caulk/Sealant
- Albis Plastics Cellulose Acetate Butyrate B9324 (UVI, Odor Mask Added), 4% Plasticizer (discontinued **)
- Lehmann & Voss LUVOCOM® 1800-8435 PET, with PTFE
- SABIC Innovative Plastics Noryl GTX GTX966 PPE+PA66 (Asia Pacific)
- Teknor Apex Tekbond® TB 1339A Thermoplastic Elastomer
- ExxonMobil Exceed™ 1018HA Metallocene Polyethylene Resin
- 3M 7904 Screen Printable Sheet Vinyl Label Material
- 3M 8427-6 Cold Shrink Connector Insulators
Copyright © lookpolymers.com All Rights Reserved