SABIC Innovative Plastics LNP STAT-KON DE003P PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-KON DE003P PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP STAT-KON* DE003P is a compound based on Polycarbonate resin containing 15% Carbon Fiber. Added features of this material include: Electrically Conductive, Exceptional Processing.
Physical Properties Metric English Comments
Density 1.25 g/cc
0.0452 lb/in³
ASTM D792
Moisture Absorption 0.150 %
0.150 %
50% RH, 24 hrs; ASTM D570
0.400 %
0.400 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.00040 - 0.0010 cm/cm

@Time 86400 sec
0.00040 - 0.0010 in/in

@Time 24.0 hour
ASTM D955
0.00040 - 0.0013 cm/cm

@Time 86400 sec
0.00040 - 0.0013 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0030 - 0.0040 cm/cm

@Time 86400 sec
0.0030 - 0.0040 in/in

@Time 24.0 hour
ASTM D955
0.0032 - 0.0041 cm/cm

@Time 86400 sec
0.0032 - 0.0041 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 110 MPa
16000 psi
ISO 527
121 MPa
17500 psi
ASTM D638
Elongation at Break 1.4 %
1.4 %
ISO 527
1.7 %
1.7 %
ASTM D638
Tensile Modulus 9.88 GPa
1430 ksi
1 mm/min; ISO 527
11.16 GPa
1619 ksi
50 mm/min; ASTM D638
Flexural Strength 184 MPa
26700 psi
ISO 178
193 MPa
28000 psi
ASTM D790
Flexural Modulus 9.77 GPa
1420 ksi
ISO 178
9.92 GPa
1440 ksi
ASTM D790
Izod Impact, Notched 0.770 J/cm
1.44 ft-lb/in
ASTM D256
Izod Impact, Unnotched 4.25 J/cm
7.96 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 33.0 kJ/m²
15.7 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 16.0 J
11.8 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 3.00 J
2.21 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 12.5 µm/m-°C

@Temperature -40.0 - 40.0 °C
6.94 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
22.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
12.4 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 49.3 µm/m-°C

@Temperature -40.0 - 40.0 °C
27.4 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
49.3 µm/m-°C

@Temperature -40.0 - 40.0 °C
27.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 145 °C
293 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
145 °C

@Thickness 3.20 mm
293 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 142 °C
288 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
142 °C

@Thickness 3.20 mm
288 °F

@Thickness 0.126 in
unannealed; ASTM D648
Electrical Properties Metric English Comments
Surface Resistance 100 - 1.00e+6 ohm
100 - 1.00e+6 ohm
ASTM D257