SABIC Innovative Plastics LNP STAT-KON DE002 PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DE002 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-Kon* DE002 is a Polycarbonate containing Carbon Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.29 g/cc | 1.29 g/cc | ASTM D792 |
| Density | 1.29 g/cc | 0.0466 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0800 % | 0.0800 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0800 % | 0.0800 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 97.0 MPa | 14100 psi | Type I, 5 mm/min; ASTM D638 |
| 97.0 MPa | 14100 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 7.2 % | 7.2 % | 5 mm/min; ISO 527 |
| 7.5 % | 7.5 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 10.34 GPa | 1500 ksi | 1 mm/min; ISO 527 |
| 11.14 GPa | 1616 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 149 MPa | 21600 psi | ISO 178 |
| 159 MPa | 23100 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 7.44 GPa | 1080 ksi | 2 mm/min; ISO 178 |
| 7.46 GPa | 1080 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Unnotched | 0.0900 J/cm | 0.169 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 32.0 kJ/m² | 15.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 26.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
14.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 58.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
32.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 146 °C @Thickness 3.20 mm |
295 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 142 °C | 288 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 141 °C @Thickness 3.20 mm |
286 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.0 - 6.0 ohm-cm | 4.0 - 6.0 ohm-cm | ASTM D257 |
| Surface Resistance | 3.0 - 5.0 ohm | 3.0 - 5.0 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 66 GF 10 PA66, 10% glass fibre
- Polykemi AB POLYfill PPH K20020 Polypropylene Homopolymer, Mineral Reinforced
- Phillips 66 COPYLENE® CH003T Polypropylene, Homopolymer, Sheet
- Styron CALIBREâ„¢ 2061-22 Polycarbonate
- Styron XZ 97222.00 SB Latex
- UBE UBESTA® 3020GX9 23% Glass Fiber Reinforced Nylon 12
- Ecomass® 1080ZB92 Filled Polyamide
- ATI Allegheny Ludlum Grade 12 Titanium (UNS R53400)
Copyright © lookpolymers.com All Rights Reserved