ExxonMobil Bicor® 380 AB OPP Film
| Category | Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Bicor® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Bicor® 380 AB OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: Bicor AB is a two-side acrylic coated, sealable OPP film designed for general use in overwrap and horizontal packaging. This film is suitable as an unsupported web or lamination. It can be surface printed, reverse printed, or sued unprinted.Availability: Latin America, North America and South AmericaKey Features:Outstanding optical propertiesRobust machinablityLow and consistent COFExcellent hot slipExcellent flavor and aroma barrierPrintable on both sidesFeatures:Acrylic CoatedFlavor & Aroma BarrierIn Lamination Lap SealableApplications:Biscuits/Cookie/CrackersBox OverwrapConfectionery, GumConfectionery, SugarTobaccoUses:Box Overwrap Flexible PackagingHFF Flexible PackagingPre-made Bags - Flexible PackagingTobacco Overwrap Flexible PackagingProcessing Method: Cold Seal Adhesive, Inner Web Adhesive Lamination, Outer Web Adhesive Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing, Surface Print Unsupported and Water-based Flexographic Printing Information provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 7.30 g/m²/day | 0.470 g/100 in²/day | 38°C, 90% RH; ExxonMobil Method |
| Thickness | 20.3 microns | 0.800 mil | Nominal; ExxonMobil Method |
| Coating Weight | 18.2 g/m² | 11.4 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Coefficient of Friction | 0.25 | 0.25 | Acrylic/Acrylic; ExxonMobil Method |
| Film Tensile Strength at Break, MD | 138 MPa | 20000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 228 MPa | 33000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 4.5 % | 4.5 % | at 275°F; ExxonMobil Method |
| Shrinkage, TD | 4.0 % | 4.0 % | at 275°F; ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.6 % | 1.6 % | ExxonMobil Method |
| Gloss | 90 % | 90 % | 45º; ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Crimp Seal MST | 185°F | |
| Crimp Seal Strength | 540 g/in | 260°F, 20psi, 3/4sec |
| Yield | 38000 in2/lb |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE D 4510 BLK
- Palm Labs Adhesives Turbo Fuse Series 130PR PLASTIC & RUBBER (100 Viscosity) Rapid Bonding Adhesive
- Special Metals INCONEL® MA758 Oxide-Dispersion-Strengthened Ni-Cr Superalloy
- A. Schulman PP 3489-01 Polypropylene Homopolymer
- Beijing Evergrow Resources CFC-DD-1000 Carbon Fiber Cloth
- Austin Novel Materials Texalan® 564D Polyether-based TPU
- Eastman D4041-P Polyethylene (discontinued **)
- Cookson Group Plaskon® 3300S Mineral Filled Novolac Epoxy Molding Compound (discontinued **)
- Bhansali Engineering Abstron BL60 Impact modifier for PVC
Copyright © lookpolymers.com All Rights Reserved