Material Notes:

LNP* LUBRICOMP* ZFL34XXC is a compound based on PPE+PS Blend resin containing Glass Fiber, PTFE. Added features incluce: Internally Lubricated.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.

Physical Properties	Metric	English	Comments
Density	1.30 g/cc	0.0470 lb/inÂ³	ISO 1183
Linear Mold Shrinkage, Flow	0.0024 cm/cm	0.0024 in/in	SABIC Method

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	91.0 MPa	13200 psi	5 mm/min; ISO 527
Elongation at Break	2.1 %	2.1 %	5 mm/min; ISO 527
Tensile Modulus	6.40 GPa	928 ksi	1 mm/min; ISO 527
Flexural Yield Strength	122 MPa	17700 psi	2 mm/min; ISO 178
Flexural Modulus	5.20 GPa	754 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	7.00 kJ/mÂ² @Temperature 23.0 Â°C	3.33 ft-lb/inÂ² @Temperature 73.4 Â°F	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	25.0 kJ/mÂ² @Temperature 23.0 Â°C	11.9 ft-lb/inÂ² @Temperature 73.4 Â°F	80104; ISO 180/1U

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	129 Â°C	264 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi)	122 Â°C	252 Â°F	Flatw 80104 sp=64mm; ISO 75/Af