SABIC Innovative Plastics LNP Lubricomp WBG16 PBT (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass Bead Filled |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Lubricomp WBG16 PBT (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* WBG16 is a compound based on Polybutylene Terephalate resin containing Glass Bead, Graphite.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.011 - 0.018 cm/cm | 0.011 - 0.018 in/in | on tensile bar; SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.7 % | 2.7 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 4.40 GPa | 638 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 86.0 MPa | 12500 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.00 GPa | 580 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 20.0 kJ/m² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 86.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
47.8 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 89.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
49.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 181 °C | 358 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C | 189 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- Rogers Corporation RO4450B Prepreg
- Chevron Phillips 7109CLT LLDPE Blown Film Resin, Hexene Copolymer (discontinued **)
- Momentive Performance Materials TSE 221-3U Heat Cured Rubber
- Techmer ES Statiblend® PPS GF40 EC BK 40% Glass Filled
- Styrolution Terluran® SP-6 ABS
- A. Schulman POLYFORT™ FPP 2496 Injection Molding Grade, Mineral Fortified Polypropylene
- A. Schulman FORMION™ FI 397 Ionomer
- DuPont Teijin Films Mylar® WC Polyester Film, 48 Gauge
- 3M #11 Roofing Granule (Corona)
- Lucite International Diakon® Frost 902 80 Acrylic Polymer
Copyright © lookpolymers.com All Rights Reserved