Dow Corning HV 1540/20P BASE AND CLEAR CURING AGENT
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) , Silicone , Silicone Rubber |
| Manufacturer | Dow Corning |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow Corning HV 1540/20P BASE AND CLEAR CURING AGENT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
32 Shore, very low viscosity, castable hydrophobic silicone rubber with high tear strength and low temperature cure.Information provided by Dow Corning
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc @Temperature 25.0 °C |
1.13 g/cc @Temperature 77.0 °F |
|
| Viscosity | 14000 cP | 14000 cP | dynamic, mixing |
| 16000 cP | 16000 cP | dynamic, part B | |
| 20000 cP | 20000 cP | dynamic, part A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 32 | 32 | |
| Tensile Strength, Ultimate | 7.79 MPa | 1130 psi | |
| Elongation at Break | 500 % | 500 % | |
| Tear Strength | 29.8 kN/m | 170 pli |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | clear; thickness not quantified |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 6.00e+14 ohm-cm | 6.00e+14 ohm-cm | |
| Dielectric Constant | 2.8 @Frequency 100 Hz |
2.8 @Frequency 100 Hz |
|
| Dielectric Strength | 24.2 kV/mm | 615 kV/in | |
| Dissipation Factor | 0.0010 @Frequency 100 Hz |
0.0010 @Frequency 100 Hz |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 10.0 min @Temperature 100 °C |
0.167 hour @Temperature 212 °F |
|
| 50.0 min @Temperature 60.0 °C |
0.833 hour @Temperature 140 °F |
||
| 1440 min @Temperature 22.0 °C |
24.0 hour @Temperature 71.6 °F |
||
| Pot Life | 60 min | 60 min | |
| Shelf Life | 6.00 Month | 6.00 Month |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | clear | part A |
| light grey | part B | |
| Hydrophobic | yes | |
| Mix Ratio (X:1) | 9 | Base to Catalyst ETN |
Users viewing this material also viewed the following:
- Potters Industries Conduct-O-Fil® S3000-S2M Silver-Coated Solid Glass Spheres
- NIZHNEKAMSKNEFTEKHIM PP 4215M (EP1X35F) Propylene and Ethylene Copolymer
- Rotuba MH Cellulose Acetate
- A. Schulman SCHULAMID® 66 MK40HI 40% Mineral Reinforced, Impact Modified 66
- ExxonMobil Escorene™ UL 04533EH2 Ethylene Vinyl Acetate Copolymer (European Grade)
- ExxonMobil Geolast® 701-87W183 Thermoplastic Elastomer
- BASF Ultraform® S2320 003 PRO POM
- Polykemi AB POLYfill PPC GF5020 PB Polypropylene Copolymer, Glass Fiber Reinforced, Chemically Coupled
- Borealis MD231U Polypropylene Compound, Mineral Filled