Polykemi AB SCANBLEND FS8 ASUV4 PC/ASA, Antistatic, Improved Weather Resistance
| Category | Polymer , Thermoplastic , ASA Polymer , Polycarbonate (PC) , Polycarbonate/ASA Alloy, Unreinforced |
| Manufacturer | Polykemi AB |
| Trade Name | SCANBLEND |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB SCANBLEND FS8 ASUV4 PC/ASA, Antistatic, Improved Weather Resistance.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | With Flow; ISO 2577 |
| 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 25 g/10 min @Load 5.00 kg, Temperature 260 °C |
25 g/10 min @Load 11.0 lb, Temperature 500 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 50.0 MPa | <= 7250 psi | ISO/R527 |
| Elongation at Yield | 7.0 % | 7.0 % | ISO/R527 |
| Flexural Strength | <= 85.0 MPa | <= 12300 psi | ISO 178 |
| Flexural Modulus | 2.50 GPa @Temperature 23.0 °C |
363 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 5.50 J/cm² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 134 °C @Load 5.001 kg |
273 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Glow Wire Test | 650 °C @Thickness 2.00 mm |
1200 °F @Thickness 0.0787 in |
IEC 695-2-1 |
Users viewing this material also viewed the following:
- Mallard Creek Polymers ROVENE® 5005 SBR Latex
- Gwent Electronic Materials C2030217D2 Aluminium for PTC paste
- Solvay TECHNYL® A 218 V30 BK 34 NG PA66, 30% glass fiber, DRY
- SABIC Innovative Plastics NORYL V01525 PPE+HIPS
- Techmer ES HiFill® PA6 GF14 HS L BK 14% Glass Filled
- Cosmic Plastics K66 Long Glass Fiber Filled Iso Diallyl Phthalate Molding Compound
- A. Schulman PP 3369-01 Polypropylene Medium-Flow Homopolymer Polypropylene
- Diamond Polymers Centrex® 925 Injection Molding Grade
- Arkema Group Evatane® 1004 VL 4E Ethylene Vinyl Acetate
Copyright © lookpolymers.com All Rights Reserved