SABIC Innovative Plastics LNP LUBRILOY UX98388 PPA

Category Polymer , Thermoplastic , Polyphthalamide (PPA)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Lubriloy
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRILOY UX98388 PPA.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRILOY* UX98388 is a compound based on Polyphthalamide resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant.
Physical Properties Metric English Comments
Density 1.12 g/cc
0.0405 lb/in³
ISO 1183
Water Absorption 0.34 %

@Time 86400 sec
 0.34 %

@Time 24.0 hour
 ISO 62-1
Linear Mold Shrinkage, Flow 0.025 cm/cm
0.025 in/in
SABIC Method
0.016 cm/cm

@Time 86400 sec
 0.016 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.016 cm/cm

@Time 86400 sec
 0.016 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 67.0 MPa
9720 psi
5 mm/min; ISO 527
Tensile Strength, Yield 72.0 MPa
10400 psi
ISO 527
78.0 MPa
11300 psi
5 mm/min; ISO 527
Elongation at Yield 6.1 %
6.1 %
5 mm/min; ISO 527
Tensile Modulus 2.60 GPa
377 ksi
1 mm/min; ISO 527
Flexural Yield Strength 106 MPa
15400 psi
2 mm/min; ISO 178
Flexural Modulus 2.40 GPa
348 ksi
2 mm/min; ISO 178
2.50 GPa
363 ksi
ISO 178
Izod Impact, Notched (ISO) 14.0 kJ/m²
6.66 ft-lb/in²
80*10*4; ISO 180/1A
Thermal Properties Metric English Comments
CTE, linear, Transverse to Flow 91.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 50.6 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 131 °C
268 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf