- Lubrizol Pellethane® 2363-65D Thermoplastic Polyurethane Elastomer
Lubrizol Pellethane® 2363-65D Thermoplastic Polyurethane Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Ether Grade |
| Manufacturer | Lubrizol (former Noveon) |
| Trade Name | Pellethane® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol Pellethane® 2363-65D Thermoplastic Polyurethane Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: USP Class VIAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Pellethane product line from Dow in 2009.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0090 cm/cm | 0.0070 - 0.0090 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.0090 cm/cm | 0.0080 - 0.0090 in/in | ASTM D955 |
| Melt Flow | 40 g/10 min @Load 5.00 kg, Temperature 224 °C |
40 g/10 min @Load 11.0 lb, Temperature 435 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 62 | 62 | ASTM D2240 |
| Tensile Strength, Ultimate | 44.5 MPa | 6450 psi | ASTM D412 |
| Elongation at Break | 450 % | 450 % | ASTM D412 |
| 50% Modulus | 0.0162 GPa | 2.35 ksi | ASTM D412 |
| 100% Modulus | 0.0200 GPa | 2.90 ksi | ASTM D412 |
| 300% Modulus | 0.0345 GPa | 5.00 ksi | ASTM D412 |
| Flexural Modulus | 0.221 GPa | 32.1 ksi | ASTM D790 |
| Tear Strength | 193 kN/m | 1100 pli | Die C; ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 105 | 105 | H22 Wheel; ASTM D1044 |
| Compression Set | 30 % @Temperature 25.0 °C, Time 79200 sec |
30 % @Temperature 77.0 °F, Time 22.0 hour |
ASTM D395 |
| 35 % @Temperature 70.0 °C, Time 79200 sec |
35 % @Temperature 158 °F, Time 22.0 hour |
ASTM D395 | |
| Tensile Set | 50 % | 50 % | Elongation set after break; ASTM D412 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 104 µm/m-°C @Temperature -80.0 - -30.0 °C |
57.8 µin/in-°F @Temperature -112 - -22.0 °F |
ASTM D696 |
| Vicat Softening Point | 107 °C | 225 °F | 120°C/hr, 9.8N; ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 204 - 221 °C | 399 - 430 °F | Extrusion |
| 210 - 227 °C | 410 - 441 °F | Molding | |
| Mold Temperature | 16.0 - 60.0 °C | 60.8 - 140 °F | |
| Drying Temperature | 99.0 - 110 °C | 210 - 230 °F | air dew point <-40°C |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® XCY620HS PC+ABS
- SABIC Innovative Plastics Lexan® BX9349 PC COPOLYMER (Asia Pacific)
- SABIC Innovative Plastics Cycolac® DL100 ABS (Europe-Africa-Middle East)
- Fiberfil® PP-61/V2 Polypropylene Copolymer, Flame Retardant, UL94 V2
- SABIC Innovative Plastics LNP STAT-KON JX89626 PES
- Teknor Apex Sinvicomp SIM 5039 Polyvinyl Chloride, Flexible
- Borealis RA130E-6015 Polypropylene Random Copolymer
- Tra-Con Tra-Bond F123MV Color Keyed High Temperature Epoxy Adhesive
- DuPont Performance Polymers Minlon® 73GM40 NC010 Nylon 6 (Unverified Data**)
- BASF Novolen® 1101 M Polypropylene
Copyright © lookpolymers.com All Rights Reserved