Lucas-Milhaupt BRAZE 852 Silver Based Cadmium Free Filler Metal

Category Metal , Nonferrous Metal , Precious Metal , Silver Alloy , Solder/Braze Alloy
Manufacturer Lucas-Milhaupt
Trade Name BRAZE
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lucas-Milhaupt BRAZE 852 Silver Based Cadmium Free Filler Metal.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Characteristics: Braze 852 is a high temperature, free flowing silver brazing filler metal usable both for torch and atmosphere furnace brazing. Due to the high flow point of this alloy, torch brazing is accomplished with Handy Hi-Temp Flux or Handy Hi-Temp Flux Boron Modified. These fluxes may also be required as a supplement when brazing parts in a controlled atmosphere furnace. Even at 2000EF a dew point of -80EF or better is required to reduce manganese oxides in hydrogen. Applications: Braze 852 is used principally for applications requiring good strength, at elevated temperatures, in service. This alloy is useful for brazing stainless steels, Stellite and Inconel. It is also effective for brazing certain complex chromium-titanium carbides and is used where carbide tools may encounter high operating temperatures in service. When parts are heat treated subsequent to brazing the high melting point of this alloy is an advantage. Specifications: This alloy conforms to the following specifications: AMS 4766, AWS A5.8 BAg-23, ASME Boiler and Pressure Vessel Code Section II-C SFA 5.8 BAg-23 Information provided by Lucas-Milhaupt, Inc.
Physical Properties Metric English Comments
Density 9.96 g/cc
0.360 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 41.4 MPa

@Temperature 649 °C
6000 psi

@Temperature 1200 °F
Type 316 Stainless Steel butt joint
55.2 MPa

@Temperature 538 °C
8000 psi

@Temperature 1000 °F
Type 316 Stainless Steel sleeve joint
62.1 MPa

@Temperature 649 °C
9000 psi

@Temperature 1200 °F
SAE 1020 Steel sleeve joint
68.9 MPa

@Temperature 649 °C
10000 psi

@Temperature 1200 °F
SAE 1020 Steel butt joint
103 MPa

@Temperature 538 °C
15000 psi

@Temperature 1000 °F
SAE 1020 Steel sleeve joint
138 MPa

@Temperature 538 °C
20000 psi

@Temperature 1000 °F
SAE 1020 Steel butt joint
145 MPa

@Temperature 427 °C
21000 psi

@Temperature 800 °F
SAE 1020 Steel sleeve joint
159 MPa

@Temperature 649 °C
23000 psi

@Temperature 1200 °F
Type 316 Stainless Steel butt joint
172 MPa

@Temperature 22.2 °C
25000 psi

@Temperature 72.0 °F
Type 316 Stainless Steel sleeve joint
172 MPa

@Temperature 22.2 °C
25000 psi

@Temperature 72.0 °F
SAE 1020 Steel sleeve joint
193 MPa

@Temperature 538 °C
28000 psi

@Temperature 1000 °F
Type 316 Stainless Steel butt joint
276 MPa

@Temperature 427 °C
40000 psi

@Temperature 800 °F
SAE 1020 Steel butt joint
317 - 345 MPa

@Temperature 22.2 °C
46000 - 50000 psi

@Temperature 72.0 °F
Type 316 Stainless Steel butt joint
359 MPa

@Temperature 22.2 °C
52000 psi

@Temperature 72.0 °F
SAE 1020 Steel butt joint
400 MPa

@Temperature 316 °C
58000 psi

@Temperature 600 °F
SAE 1020 Steel butt joint
427 MPa

@Temperature 204 °C
62000 psi

@Temperature 400 °F
SAE 1020 Steel butt joint
Thermal Properties Metric English Comments
Melting Point 960 - 971 °C
1760 - 1780 °F
Solidus 960 °C
1760 °F
Melting Point
Liquidus 971 °C
1780 °F
Flow Point
Component Elements Properties Metric English Comments
Manganese, Mn >= 13.85 %
>= 13.85 %
Other, total <= 0.15 %
<= 0.15 %
Silver, Ag 84 - 86 %
84 - 86 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000375 ohm-cm
0.0000375 ohm-cm
Processing Properties Metric English Comments
Processing Temperature 971 - 1040 °C
1780 - 1900 °F
Brazing Range
Descriptive Properties Value Comments
Color White