SABIC Innovative Plastics LNP LUBRICOMP UFL36S PPA (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP UFL36S PPA (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* UFL36S is a compound based on Polyphthalamide resin containing Glass Fiber, PTFE. Added features of this material include: Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ASTM D792 |
| 1.55 g/cc | 0.0560 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.330 % | 0.330 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0017 cm/cm @Time 86400 sec |
0.0017 in/in @Time 24.0 hour |
ISO 294 |
| 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Time 86400 sec |
0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0082 cm/cm @Time 86400 sec |
0.0082 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 196 MPa | 28400 psi | ASTM D638 |
| 196 MPa | 28400 psi | ISO 527 | |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| 2.5 % | 2.5 % | ISO 527 | |
| Tensile Modulus | 9.88 GPa | 1430 ksi | 1 mm/min; ISO 527 |
| 12.41 GPa | 1800 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 280 MPa | 40600 psi | ASTM D790 |
| 286 MPa | 41500 psi | ISO 178 | |
| Flexural Modulus | 10.82 GPa | 1569 ksi | ASTM D790 |
| 11.23 GPa | 1629 ksi | ISO 178 | |
| Izod Impact, Notched | 1.17 J/cm | 2.19 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.14 J/cm | 19.00 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 70.0 kJ/m² | 33.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J | 5.16 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.46 | 0.46 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.49 | 0.49 | ASTM D3702 Modified |
| K (wear) Factor | 12.1 x 10-8 mm³/N-M | 6.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 260 °C @Thickness 3.20 mm |
500 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® HPX8R PC Copolymer (Europe-Africa-Middle East)
- SABIC Innovative Plastics Lexan® LUX9612G PC (Asia Pacific)
- Lucent Polymers PBT-FR310 Polybutylene Terephthalate, Flame Resistant
- Shakespeare FN-29 Freshwater Nylon Copolymer Fishing Line, 17 lb
- Techmer ES Electrablend® PC C BK
- SABIC Innovative Plastics Valox® VX5005 PBT (Europe-Africa-Middle East)
- SCG Chemicals EL-Leneâ„¢ L1810F Linear Low Density Polyethylene Film
- Polyram PlusTek PA4801G6 Nylon 6.6, 30% Glass Fiber Reinforced, PTFE lubricated
- China Tungsten YWR2 Tungsten Carbide with Rare Earth Additive
- BASF Ultramid® 8253 HS PA6 (Conditioned)
Copyright © lookpolymers.com All Rights Reserved