Cossa Polimeri ESTALUX 9202 A Methyl Methacrylate Acrylonitrile Butadiene Styrene
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylic (PMMA) |
| Manufacturer | Cossa Polimeri S.r.L. |
| Trade Name | ESTALUX |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cossa Polimeri ESTALUX 9202 A Methyl Methacrylate Acrylonitrile Butadiene Styrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Plastic blend that combines impact properties of ABS with the excellent transparency of PMMAInformation provided by Cossa Polimeri S.r.l.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D 955 |
| Melt Flow | 2.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
2.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D 1238 |
| 18 g/10 min @Load 21.6 kg, Temperature 220 °C |
18 g/10 min @Load 47.6 lb, Temperature 428 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 35.0 MPa | 5080 psi | ASTM D 638 |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | ASTM D 638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D 638 |
| Tensile Modulus | 2.05 GPa | 297 ksi | ASTM D 638 |
| Flexural Modulus | 1.90 GPa | 276 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.800 J/cm @Temperature 23.0 °C |
1.50 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 95.0 °C @Load 5.10 kg |
203 °F @Load 11.2 lb |
120°C/hr; ASTM D 1525 |
| 108 °C @Load 1.02 kg |
226 °F @Load 2.25 lb |
120°C/hr; ASTM D 1525 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 220 - 240 °C | 428 - 464 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Dry Time | 2.00 - 4.00 hour @Temperature 80.0 °C |
2.00 - 4.00 hour @Temperature 176 °F |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® LGN1500 PC (Asia Pacific)
- Plasma Coatings 500-H Surface Material
- Kinlead PT12 Adhesive Tape Grade BOPP Plain Film (thickness: 25 µm)
- Styrolution Novodur® H702 ABS
- CTC X-PRO PP 100 P1015 Polypropylene Homopolymer
- ExxonMobil 630 Mobil SHC 600 Series
- Beijing Ranger Chem 144 Semi Solid Epoxy Resin
- Parker Chomerics CHO-BOND 2167 Part B Silicone
- Bhansali Engineering Abstron HI40H ABS Injection Molding Grade
Copyright © lookpolymers.com All Rights Reserved