SABIC Innovative Plastics LNP LUBRICOMP RFN169 PA 66

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP RFN169 PA 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* LUBRICOMP* RFN169 is a compound based on Nylon 66 containing 30% Glass Fiber, 5% MOS2. Added features of this grade include: Wear Resistant, Flame Retardant.
Physical Properties Metric English Comments
Specific Gravity 1.68 g/cc
1.68 g/cc
ASTM D792
Density 1.67 g/cc
0.0603 lb/in³
ASTM D792
Moisture Absorption 0.400 %
0.400 %
50% RH, 24 hrs; ASTM D570
0.570 %
0.570 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0020 - 0.0050 cm/cm

@Time 86400 sec
 0.0020 - 0.0050 in/in

@Time 24.0 hour
 ASTM D955
Linear Mold Shrinkage, Transverse 0.0090 - 0.020 cm/cm

@Time 86400 sec
 0.0090 - 0.020 in/in

@Time 24.0 hour
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 190 MPa
27600 psi
5 mm/min; ISO 527
194 MPa
28100 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 2.0 %
2.0 %
Type I, 5 mm/min; ASTM D638
2.0 %
2.0 %
5 mm/min; ISO 527
Tensile Modulus 14.04 GPa
2036 ksi
1 mm/min; ISO 527
14.16 GPa
2054 ksi
50 mm/min; ASTM D638
Flexural Strength 263 MPa
38100 psi
1.3 mm/min, 50 mm span; ASTM D790
266 MPa
38600 psi
ISO 178
Flexural Modulus 12.12 GPa
1758 ksi
2 mm/min; ISO 178
12.3 GPa
1780 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 1.05 J/cm
1.97 ft-lb/in
ASTM D256
Izod Impact, Unnotched 8.66 J/cm
16.2 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 11.0 kJ/m²
5.23 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 51.0 kJ/m²
24.3 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 6.00 J

@Temperature 23.0 °C
 4.43 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.41
0.41
ASTM D3702 Modified
Coefficient of Friction, Static 0.41
0.41
ASTM D3702 Modified
K (wear) Factor 12.1 x 10-8 mm³/N-M
6.00 x 10-10 in³-min/ft-lb-hr
Ring; ASTM D3702 Modified
1010 x 10-8 mm³/N-M
503 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 28.7 µm/m-°C

@Temperature -30.0 - 30.0 °C
 15.9 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D696
CTE, linear, Transverse to Flow 76.3 µm/m-°C

@Temperature -30.0 - 30.0 °C
 42.4 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 257 °C
495 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
258 °C

@Thickness 3.20 mm
 496 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 242 °C
468 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
248 °C

@Thickness 3.20 mm
 478 °F

@Thickness 0.126 in
 unannealed; ASTM D648