SABIC Innovative Plastics LNP LUBRICOMP RCL26 PA6.6
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RCL26 PA6.6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* RCL26 is a compound based on Nylon 66 containing 30% Carbon Fiber, 10% PTFE. Added features of this grade include: Wear Resistant, Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ASTM D792 |
| Density | 1.34 g/cc | 0.0484 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.580 % | 0.580 % | 50% RH, 24 hrs; ASTM D570 |
| 0.790 % | 0.790 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 236 MPa | 34200 psi | 5 mm/min; ISO 527 |
| 243 MPa | 35200 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.8 % | 1.8 % | 5 mm/min; ISO 527 |
| 1.9 % | 1.9 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 23.25 GPa | 3372 ksi | 1 mm/min; ISO 527 |
| 24.24 GPa | 3516 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 332 MPa | 48200 psi | ISO 178 |
| 356 MPa | 51600 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 18.95 GPa | 2748 ksi | 2 mm/min; ISO 178 |
| 19.1 GPa | 2770 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.840 J/cm | 1.57 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.67 J/cm | 16.2 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 52.0 kJ/m² | 24.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J @Temperature 23.0 °C |
4.43 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.41 | 0.41 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.33 | 0.33 | ASTM D3702 Modified |
| K (wear) Factor | 86.6 x 10-8 mm³/N-M | 43.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 18.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
10.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 43.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
23.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 260 °C @Thickness 3.20 mm |
500 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 254 °C @Thickness 3.20 mm |
489 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 243 PC
- Solvay Specialty Polymers Ixef® GS-1022 Polyarylamide (PARA) (Unverified Data**)
- SABIC Innovative Plastics Ultem 2410F PEI (Europe-Africa-Middle East)
- Shandong Dongyue Shenzhou New Material Co CHF080 Perfluorosulfonic Acid Ion-Exchange Resin (PFSA)
- Saint-Gobain CHR® 2905-7R Glass Cloth Backing Silicone Adhesive Pressure Sensitive Tape
- Silberline Sparkle Silver® 3130-AR
- A. Schulman CP810-01 Natural Linear, Low-Density Polyethylene
- Asahi Kasei Leona® 1502 Nylon 66
- DuPont Elvaloy® HP443 Ethylene/N-Butyl Acrylate/Carbon Monoxide Copolymer (discontinued **)
- Reade Advanced Materials Wood's Metal Alloy (Sn + Pb + Bi + Cd)
Copyright © lookpolymers.com All Rights Reserved