ExxonMobil Oppalyte™ 35MW647 OPP Film

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer Exxon Chemical
Trade Name Oppalyte™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Oppalyte™ 35MW647 OPP Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: A super white opaque biaxially oriented polypropylene film acrylic coated two sides. Provides outstanding performances on all types of packaging machines.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Outstanding opacity, white background and reduced show-throughBroad sealing range on both sidesGood aroma and moisture barriersExcellent light barrierHigh yieldGood stiffnessSolvent-free coatingsIdeal support for water based ink printingExcellent hot tackPrintable both sidesFeatures: Acrylic CoatedFlavor & Aroma BarrierIn Lamination Lap SealableLight BarrierApplications:BakeryBiscuits/Cookie/Crackers Box OverwrapConfectionery, ChocolateConfectionery, GumConfectionery, SugarCrisps and SnacksDry Foods and Beverage Powders Health and Beauty CareHousehold Detergents Uses:Box Overwrap Flexible Packaging HFFS Flexible Packaging Pre-made Bags – Flexible PackagingVFFS Flexible PackagingProcessing Method: Cold Seal Adhesive, Inner Web Adhesive Lamination, Outer Web Adhesive Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing and Surface Print UnsupportedInformation provided by ExxonMobil
Physical Properties Metric English Comments
Water Vapor Transmission 1.30 g/m²/day

@Temperature 23.0 °C
0.0840 g/100 in²/day

@Temperature 73.4 °F
85% RH; ExxonMobil Method
6.05 g/m²/day

@Temperature 38.0 °C
0.390 g/100 in²/day

@Temperature 100 °F
90% RH; ExxonMobil Method
Oxygen Transmission Rate 900 cc/m²/day

@Temperature 23.0 °C
58.0 cc/100 in²/day

@Temperature 73.4 °F
0% RH; ExxonMobil Method
902 cc/m²/day

@Temperature 23.0 °C
58.1 cc/100 in²/day

@Temperature 73.4 °F
Wet, 75% RH; ExxonMobil Method
Thickness 35.6 microns
1.40 mil
ExxonMobil Method
Coating Weight 22.1 g/m²
13.8 lb/ream
ExxonMobil Method
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 140 %
140 %
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Elongation at Break, TD 50 %
50 %
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Modulus of Elasticity 1.30 GPa
189 ksi
MD; ExxonMobil Method
2.10 GPa
305 ksi
TD; ExxonMobil Method
Coefficient of Friction 0.25
0.25
Both Sides; ExxonMobil Method
Seal Strength 410 g/25 mm

@Pressure 0.276 MPa,
Temperature 130 °C
410 g/in

@Pressure 40.0 psi,
Temperature 266 °F
Otto Brugger, 0.2 sec; ExxonMobil Method
Film Tensile Strength at Break, MD 100 MPa
14500 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD 155 MPa
22500 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Thermal Properties Metric English Comments
Shrinkage, MD 5.0 %

@Temperature 135 °C,
Time 432 sec
5.0 %

@Temperature 275 °F,
Time 0.120 hour
ExxonMobil Method
Shrinkage, TD 5.0 %

@Temperature 135 °C,
Time 432 sec
5.0 %

@Temperature 275 °F,
Time 0.120 hour
ExxonMobil Method
Optical Properties Metric English Comments
Gloss 75 %
75 %
45°; ExxonMobil Method
Transmission, Visible 22 %
22 %
ExxonMobil Method
Descriptive Properties Value Comments
Heat Seal Range 90°F
36.3 psi, 0.2 sec
Whiteness Index 80
Yield 31200 in2/lb