Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

SABIC Innovative Plastics LNP LUBRICOMP KP004L Acetal Copoly (Asia Pacific)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP KP004L Acetal Copoly (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* KP004L is a compound based on Acetal Copolymer resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated, Low Extractible.
Physical Properties Metric English Comments
Density 1.48 g/cc
0.0535 lb/in³
ISO 1183
1.48 g/cc
0.0535 lb/in³
ASTM D792
Moisture Absorption 0.200 %
0.200 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.029 cm/cm

@Time 86400 sec
 0.029 in/in

@Time 24.0 hour
 ISO 294
0.028 - 0.030 cm/cm

@Time 86400 sec
 0.028 - 0.030 in/in

@Time 24.0 hour
 ASTM D955
Linear Mold Shrinkage, Transverse 0.024 cm/cm

@Time 86400 sec
 0.024 in/in

@Time 24.0 hour
 ISO 294
0.023 - 0.025 cm/cm

@Time 86400 sec
 0.023 - 0.025 in/in

@Time 24.0 hour
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 46.0 MPa
6670 psi
ASTM D638
46.0 MPa
6670 psi
ISO 527
Tensile Strength, Yield 47.0 MPa
6820 psi
ASTM D638
47.0 MPa
6820 psi
ISO 527
Elongation at Break 34.3 %
34.3 %
ISO 527
39.6 %
39.6 %
ASTM D638
Elongation at Yield 19.2 %
19.2 %
ISO 527
20.2 %
20.2 %
ASTM D638
Tensile Modulus 2.06 GPa
299 ksi
50 mm/min; ASTM D638
2.27 GPa
329 ksi
1 mm/min; ISO 527
Flexural Strength 119 MPa
17300 psi
ISO 178
Flexural Modulus 2.06 GPa
299 ksi
ASTM D790
5.40 GPa
783 ksi
ISO 178
Izod Impact, Notched 0.530 J/cm
0.993 ft-lb/in
ASTM D256
Izod Impact, Unnotched 7.15 J/cm
13.4 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 46.0 kJ/m²
21.9 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 5.00 J
3.69 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 1.00 J
0.738 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.27
0.27
ASTM D3702 Modified
Coefficient of Friction, Static 0.15
0.15
ASTM D3702 Modified
K (wear) Factor 18.1 x 10-8 mm³/N-M
9.00 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 117 µm/m-°C

@Temperature -40.0 - 40.0 °C
 65.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
118 µm/m-°C

@Temperature -40.0 - 40.0 °C
 65.6 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 117 µm/m-°C

@Temperature -40.0 - 40.0 °C
 65.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
117 µm/m-°C

@Temperature -40.0 - 40.0 °C
 65.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 145 °C
293 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
151 °C

@Thickness 3.20 mm
 304 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 88.0 °C
190 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
81.0 °C

@Thickness 3.20 mm
 178 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Users viewing this material also viewed the following:
Copyright © lookpolymers.com All Rights Reserved