SABIC Innovative Plastics LNP LUBRICOMP KFI12 Acetal Copolymer
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 10% Glass Fiber Reinforced |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP KFI12 Acetal Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* KFI12 is a compound based on Acetal Copolymer resin containing 10% Glass Fiber, 2% Silicone. Added feature of this grade is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ASTM D792 |
| Density | 1.44 g/cc | 0.0520 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.250 % | 0.250 % | 50% RH, 24 hrs; ASTM D570 |
| 0.340 % | 0.340 % | 23°C / 50% RH; ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 56.0 MPa | 8120 psi | Type I, 5 mm/min; ASTM D638 |
| 58.0 MPa | 8410 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | Type I, 5 mm/min; ASTM D638 |
| 62.0 MPa | 8990 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.6 % | 2.6 % | 5 mm/min; ISO 527 |
| 3.3 % | 3.3 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 2.3 % | 2.3 % | Type I, 5 mm/min; ASTM D638 |
| 2.3 % | 2.3 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 4.78 GPa | 693 ksi | 1 mm/min; ISO 527 |
| 4.91 GPa | 712 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 91.0 MPa | 13200 psi | ISO 178 |
| Flexural Yield Strength | 91.0 MPa | 13200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 4.07 GPa | 590 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 4.14 GPa | 600 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.540 J/cm | 1.01 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.17 J/cm | 7.81 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 26.0 kJ/m² | 12.4 ft-lb/in² | 80*10*3; ISO 180/1U |
| Dart Drop, Total Energy | 5.00 J @Temperature 23.0 °C |
3.69 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 83.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
46.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
50.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C | 324 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 163 °C @Thickness 3.20 mm |
325 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 159 °C | 318 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 161 °C @Thickness 3.20 mm |
322 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne OnFlex™ S KG 70A-3S2019 Thermoplastic Elastomer (TPE)
- Mitsui AURUM® JCN6230 Thermoplastic Polyimide Resin, Crystalline (discontinued **)
- Ineos ABS Lustran® Ultra 4105 ABS Pellets (Polycarbonate-modified), Medium High Heat Grade
- SABIC Innovative Plastics ULTEM 2212EPR PEI
- Silon Taborex TA 1131 HD Chemically-Crosslinkable HDPE Compound
- Toyobo Vylopet® EMC145 Glass Reinforced Polyester, Standard Grade
- Unitika TERRAMAC HV-6250H Polylactic Acid (PLA)
- Eastman Tenite 360E2R30016 Cellulose Acetate Propionate, Natural, Trsp
- BASF Ultramid® A3X2G7 35% Glass Filled PA66 (Dry)
Copyright © lookpolymers.com All Rights Reserved