SABIC Innovative Plastics LNP LUBRICOMP GFL36L PSU (Asia Pacific)

Category	Polymer , Thermoplastic , Polysulfone (PSU)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP LUBRICOMP
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP LUBRICOMP GFL36L PSU (Asia Pacific).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* Lubricomp* GFL36L is a compound based on Polysulfone resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Low Extractible.

Physical Properties	Metric	English	Comments
Density	1.62 g/cc	0.0585 lb/inÂ³	ASTM D792
	1.62 g/cc	0.0585 lb/inÂ³	ISO 1183
Moisture Absorption	0.100 %	0.100 %	50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow	0.0026 cm/cm @Time 86400 sec	0.0026 in/in @Time 24.0 hour	ISO 294
	0.0020 - 0.0040 cm/cm @Time 86400 sec	0.0020 - 0.0040 in/in @Time 24.0 hour	ASTM D955
Linear Mold Shrinkage, Transverse	0.0040 - 0.0060 cm/cm @Time 86400 sec	0.0040 - 0.0060 in/in @Time 24.0 hour	ASTM D955
	0.0051 cm/cm @Time 86400 sec	0.0051 in/in @Time 24.0 hour	ISO 294

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	87.0 MPa	12600 psi	ISO 527
	88.0 MPa	12800 psi	ASTM D638
Tensile Strength, Yield	87.0 MPa	12600 psi	ISO 527
	88.0 MPa	12800 psi	ASTM D638
Elongation at Break	1.2 %	1.2 %	ISO 527
	1.3 %	1.3 %	ASTM D638
Elongation at Yield	1.3 %	1.3 %	ASTM D638
	1.3 %	1.3 %	ISO 527
Tensile Modulus	9.33 GPa	1350 ksi	1 mm/min; ISO 527
	10.34 GPa	1500 ksi	50 mm/min; ASTM D638
Flexural Strength	110 MPa	16000 psi	ASTM D790
	121 MPa	17500 psi	ISO 178
Flexural Modulus	8.96 GPa	1300 ksi	ASTM D790
	9.00 GPa	1310 ksi	ISO 178
Izod Impact, Notched	0.740 J/cm	1.39 ft-lb/in	ASTM D256
Izod Impact, Unnotched	3.41 J/cm	6.39 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	8.00 kJ/mÂ²	3.81 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	23.0 kJ/mÂ²	10.9 ft-lb/inÂ²	80104; ISO 180/1U
Dart Drop, Total Energy	14.0 J	10.3 ft-lb	Instrumented Impact Energy @ peak; ASTM D3763
Impact Test	3.00 J	2.21 ft-lb	Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic	0.42	0.42	ASTM D3702 Modified
Coefficient of Friction, Static	0.62	0.62	ASTM D3702 Modified
K (wear) Factor	88.6 x 10^-8 mmÂ³/N-M	44.0 x 10^-10 inÂ³-min/ft-lb-hr	Washer; ASTM D3702 Modified

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	30.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	16.7 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
	30.6 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	17.0 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
CTE, linear, Transverse to Flow	24.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	13.3 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
	25.2 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	14.0 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi)	186 Â°C	367 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
	185 Â°C @Thickness 3.20 mm	365 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	181 Â°C	358 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	180 Â°C @Thickness 3.20 mm	356 Â°F @Thickness 0.126 in	unannealed; ASTM D648