- HOME
- POLYMER SEARCH
- Thermoplastic
- Polyetherimide (PEI)
- SABIC Innovative Plastics LNP LUBRICOMP ECL36XXQ PEI
SABIC Innovative Plastics LNP LUBRICOMP ECL36XXQ PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP ECL36XXQ PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* ECL36XXQ is a compound based on Polyetherimide containing 30% Carbon Fiber, 15% PTFE. Added features of this material include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.39 g/cc | 1.39 g/cc | ASTM D792 |
| Density | 1.39 g/cc | 0.0502 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.00010 - 0.00050 cm/cm @Time 86400 sec |
0.00010 - 0.00050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0010 - 0.0040 cm/cm @Time 86400 sec |
0.0010 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 222 MPa | 32200 psi | Type I, 5 mm/min; ASTM D638 |
| 226 MPa | 32800 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 0.90 % | 0.90 % | Type I, 5 mm/min; ASTM D638 |
| 1.0 % | 1.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 30.42 GPa | 4412 ksi | 1 mm/min; ISO 527 |
| 32.86 GPa | 4766 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 324 MPa | 47000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 26.3 GPa | 3810 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Poissons Ratio | 0.43 | 0.43 | ASTM E 132 |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.13 J/cm | 7.74 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 11.0 J @Temperature 23.0 °C |
8.11 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Coefficient of Friction, Dynamic | 0.39 | 0.39 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.42 | 0.42 | ASTM D3702 Modified |
| K (wear) Factor | 44.3 x 10-8 mm³/N-M | 22.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C @Thickness 3.20 mm |
406 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 10000 ohm | 100 - 10000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufGuard M™ GPP1005M-CD PP, Flame Retardant
- Technetics Group Amicon™ PEEK (Unverified Data**)
- Overview of materials for Polycarbonate, Optical Grade
- SABIC Innovative Plastics Lexan® SLX1432 PC Copolymer (Asia Pacific)
- ICO Polymers ICORENEâ„¢ 150-1500 HDPE Rotational Molding Resin
- SABIC Innovative Plastics ULTEM 3452 PEI (Asia Pacific)
- Techmer ES Electrafil® J-50/CF/30/TF/13/SI/2 Polycarbonate, 30% Carbon Fiber Reinforced, 13% PTFE, 2% Silicone
- Chase Plastics CP Pryme® N120GL (DAM) Nylon 6, 20% Glass Fiber Reinforced, Internally Lubricated