Westlake LF2050 Hexene Linear Low Density Polyethylene

Category	Polymer , Thermoplastic , Polyethylene (PE) , LLDPE
Manufacturer	Westlake Chemical Corporation
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Westlake LF2050 Hexene Linear Low Density Polyethylene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Westlake LF2050 is a hexene LLDPE with excellent physical properties and heat sealing characteristics, which allow for down-gauging and blending with other materials. Typical applications include stretch films, heavy duty bags and sacks, agricultural films, and trash bags & liners. This Kosher compliant material is available with various slip and antiblock levels.Application/UsesBags and sacksAgricultural filmsTrash bags and linersCo-extruded structuresFDA: This material complies with FDA regulations in 21 CFR, section 177.1520. Kosher Compliant.All information provided by Westlake Chemical

Physical Properties	Metric	English	Comments
Density	0.918 g/cc	0.0332 lb/in³	ASTM D1505
Thickness	25.4 microns	1.00 mil
Melt Flow	3.5 g/10 min	3.5 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	9.65 MPa	1400 psi
Film Tensile Strength at Yield, TD	9.65 MPa	1400 psi
Film Elongation at Break, MD	500 %	500 %	ASTM D882
Film Elongation at Break, TD	850 %	850 %	ASTM D882
Elmendorf Tear Strength, MD	6.69 g/micron	170 g/mil
Elmendorf Tear Strength, TD	18.1 g/micron	460 g/mil
Dart Drop	3.74 g/micron	95.0 g/mil	ASTM D1709
Film Tensile Strength at Break, MD	50.3 MPa	7300 psi	ASTM D882
Film Tensile Strength at Break, TD	33.8 MPa	4900 psi	ASTM D882
1% Secant Modulus, MD	138 MPa	20000 psi	ASTM D882
1% Secant Modulus, TD	152 MPa	22000 psi	ASTM D882

Optical Properties	Metric	English	Comments
Haze	1.5 %	1.5 %	ASTM D1003
Gloss	95 %	95 %	45°

Processing Properties	Metric	English	Comments
Melt Temperature	204 - 216 °C	400 - 420 °F
Blow-up Ratio (BUR)	2.5	2.5

Descriptive Properties	Value	Comments
Process	Film