SABIC Innovative Plastics LNP LUBRICOMP DX00714H PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP DX00714H PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* DX00714H is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ASTM D792 |
| 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| 0.120 % | 0.120 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 89.0 MPa | 12900 psi | ASTM D638 |
| 90.0 MPa | 13100 psi | ISO 527 | |
| Elongation at Break | 2.2 % | 2.2 % | ASTM D638 |
| 3.3 % | 3.3 % | ISO 527 | |
| Tensile Modulus | 6.34 GPa | 920 ksi | 1 mm/min; ISO 527 |
| 6.55 GPa | 950 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 135 MPa | 19600 psi | ISO 178 |
| 137 MPa | 19900 psi | ASTM D790 | |
| Flexural Modulus | 5.20 GPa | 754 ksi | ISO 178 |
| 5.31 GPa | 770 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.740 J/cm | 1.39 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.36 J/cm | 6.29 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 30.0 J | 22.1 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 72.0 J | 53.1 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.46 | 0.46 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.51 | 0.51 | ASTM D3702 Modified |
| K (wear) Factor | 888 x 10-8 mm³/N-M | 441 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 140 °C @Thickness 3.20 mm |
284 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3825 TPE, PP Overmold or Standalone use
- Plastcom SLOVALEN PH 91 T 20 Polypropylene Homopolymer, 20% Micronized Talc
- Polymer Resources PC/ABS-FR1-[color]-HH Flame Retardant PC/ABS Alloy, Low Flow
- SABIC Innovative Plastics LNP Verton RV008ESV PA 66
- Solvay SUPRAGIL® MNS/90 Condensed methyl naphthalene sulfonate, sodium salt
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 45 PHR N220 Filler
- EMS-Grivory Grivory® FG 40 NL nat 6025 PA6
- DSM Stanyl® TW271F6 Nylon 46-30% Glass Reinforced (European and Asian Grade) (Cond)
- Polikim KESTAMID® HS Polyamide 6, Heat Resistant
- Ascend Performance Materials Vydyne® R513H Nylon 66, 13% Glass Filled, Dry as Molded
Copyright © lookpolymers.com All Rights Reserved