SABIC Innovative Plastics LNP LUBRICOMP DL003E PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP DL003E PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* DL003E is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Easy Molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ASTM D792 |
| 1.29 g/cc | 0.0466 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.0090 cm/cm @Time 86400 sec |
0.0080 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.0090 cm/cm @Time 86400 sec |
0.0080 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ASTM D638 |
| 50.0 MPa | 7250 psi | ISO 527 | |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | ASTM D638 |
| 54.0 MPa | 7830 psi | ISO 527 | |
| Elongation at Break | 9.6 % | 9.6 % | ISO 527 |
| 25.5 % | 25.5 % | ASTM D638 | |
| Elongation at Yield | 5.5 % | 5.5 % | ISO 527 |
| 5.6 % | 5.6 % | ASTM D638 | |
| Tensile Modulus | 2.18 GPa | 316 ksi | 50 mm/min; ASTM D638 |
| 2.20 GPa | 319 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 82.0 MPa | 11900 psi | ASTM D790 |
| 84.0 MPa | 12200 psi | ISO 178 | |
| Flexural Modulus | 2.30 GPa | 334 ksi | ASTM D790 |
| 2.30 GPa | 334 ksi | ISO 178 | |
| Izod Impact, Notched | 1.43 J/cm | 2.68 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 21.36 J/cm | 40.02 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 16.0 kJ/m² | 7.61 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 100 kJ/m² | 47.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.18 | 0.18 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.070 | 0.070 | ASTM D3702 Modified |
| K (wear) Factor | 121 x 10-8 mm³/N-M | 60.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 73.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
41.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 74.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
41.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 75.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
41.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 75.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
41.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 138 °C | 280 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C | 262 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 116 °C @Thickness 3.20 mm |
241 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Ineos Nova 765 High Performance Styrenic Enhanced Polystyrene (discontinued **)
- SABIC Innovative Plastics Lexan® SLX2432T PC Copolymer
- Techmer ES Electrablend® PA6/6 IM C BK
- Solvay Specialty Polymers AvaSpire® AV-722 SL30 Polyaryletherketone (PAEK)
- Solvay TECHNYL® A 20 V35 PA66, 35% glass fiber, Conditioned
- Westlake Plastics Propylux® 290 Polypropylene, Heat Stabilized
- Bhansali Engineering Abstron HR-60 ABS Heat Resistant
- Austin Novel Materials Texalan® 395A Polyester-based TPU
- Resinlab® EP1112 Black Electronic Grade Epoxy Encapsulant
Copyright © lookpolymers.com All Rights Reserved