SABIC Innovative Plastics LNP LUBRICOMP DFL32XXC PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP DFL32XXC PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* DFL32XXC is a compound based on Polycarbonate resin containing 10% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.110 % | 0.110 % | 50% RH, 24 hrs; ASTM D570 |
| 0.170 % | 0.170 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0023 cm/cm @Time 86400 sec |
0.0023 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0067 cm/cm @Time 86400 sec |
0.0067 in/in @Time 24.0 hour |
ISO 294 |
| 0.0070 cm/cm @Time 86400 sec |
0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 71.0 MPa | 10300 psi | ISO 527 |
| 73.0 MPa | 10600 psi | ASTM D638 | |
| Elongation at Break | 2.8 % | 2.8 % | ISO 527 |
| 3.1 % | 3.1 % | ASTM D638 | |
| Tensile Modulus | 4.28 GPa | 621 ksi | 1 mm/min; ISO 527 |
| 4.35 GPa | 631 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 114 MPa | 16500 psi | ISO 178 |
| 123 MPa | 17800 psi | ASTM D790 | |
| Flexural Modulus | 4.17 GPa | 605 ksi | ISO 178 |
| 4.35 GPa | 631 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.900 J/cm | 1.69 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.34 J/cm | 10.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 34.0 kJ/m² | 16.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 11.0 J | 8.11 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 141 °C @Thickness 3.20 mm |
286 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- 3M Dyneon™ Fluorel™ FE-5641Q Fluoroelastomer VF2 + HFP Dipolymer (discontinued **)
- Polimeri Europa Extir® P 1212 Expandable Polystyrene (discontinued **)
- Multibase Multi-Flex® A 7005 C TPE Thermoplastic Elastomer
- Samyang Trirex® PC-3022IR 15 MFI Clear Polycarbonate With Release
- Sumitomo Bakelite North America 52-20-30 Short-Glass Reinforced Diallyl Phthalate
- A. Schulman PP 2175 Polypropylene High Flow Copolymer Polypropylene
- Universal Wire Works 17-7 (AMS 5824) Filler Metal
- DuPont Elvax® 3172Z Ethylene Vinyl Acetate (discontinued **)
- MetalTek MTEK H46 Martensitic Stainless Steel
Copyright © lookpolymers.com All Rights Reserved