SABIC Innovative Plastics LNP LUBRICOMP JCL36E PES
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP JCL36E PES.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* JCL36E is a compound based on Polyethersulfone (PES) resin containing 30% Carbon Fiber, 15% PTFE. Added feature of this grade is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.55 g/cc | 1.55 g/cc | ASTM D792 |
| Density | 1.54 g/cc | 0.0556 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0200 % | 0.0200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0400 % | 0.0400 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.00010 - 0.00030 cm/cm @Time 86400 sec |
0.00010 - 0.00030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 142 MPa | 20600 psi | Type I, 5 mm/min; ASTM D638 |
| 145 MPa | 21000 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 142 MPa | 20600 psi | Type I, 5 mm/min; ASTM D638 |
| 145 MPa | 21000 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 0.50 % | 0.50 % | Type I, 5 mm/min; ASTM D638 |
| 0.50 % | 0.50 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 0.50 % | 0.50 % | Type I, 5 mm/min; ASTM D638 |
| 0.50 % | 0.50 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 26.32 GPa | 3817 ksi | 1 mm/min; ISO 527 |
| 26.88 GPa | 3899 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 198 MPa | 28700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 213 MPa | 30900 psi | ISO 178 | |
| Flexural Yield Strength | 199 MPa | 28900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 22.88 GPa | 3318 ksi | 2 mm/min; ISO 178 |
| 23.4 GPa | 3390 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.580 J/cm | 1.09 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.17 J/cm | 5.94 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Dart Drop, Total Energy | 5.00 J @Temperature 23.0 °C |
3.69 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Coefficient of Friction, Dynamic | 0.34 | 0.34 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.36 | 0.36 | ASTM D3702 Modified |
| K (wear) Factor | 50.4 x 10-8 mm³/N-M | 25.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 13.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
7.22 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 27.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
15.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 280 °C | 536 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 279 °C @Thickness 3.20 mm |
534 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 270 °C | 518 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 270 °C @Thickness 3.20 mm |
518 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Qualchem Danamid AFGFS2HUV30 Polyamide 66, 30% Glass Fiber
- Karina 32/82-FC-(CS) Orange Color Concentrate for PVC
- H.C. Starck MoCu 80/20 Molybdenum-Copper Composite Material
- Teknor Apex TruVis Esters™ TNTM TriNonyl Trimellitate
- DuPont Teijin Films Mylar® EL Polyester Film, 500 Gauge
- A. Schulman POLYFORT™ PP 3701
Copyright © lookpolymers.com All Rights Reserved