SABIC Innovative Plastics LNP KONDUIT PX11313 PA 6 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Konduit |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP KONDUIT PX11313 PA 6 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Thermally conductive mineral and glass fiber filled PA6, FR, compliant with ECO protocols, non-brominated, non-chlorinated
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.79 g/cc | 0.0647 lb/in³ | ISO 1183 |
| Melt Index of Compound | 21 g/10 min @Load 10.0 kg, Temperature 300 °C |
21 g/10 min @Load 22.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 105 MPa | 15200 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.3 % | 1.3 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 15.0 GPa | 2180 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 160 MPa | 23200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 13.0 GPa | 1890 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 22.0 kJ/m² | 10.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.5 µm/m-°C @Temperature 40.0 - 120 °C |
22.5 µin/in-°F @Temperature 104 - 248 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 85.4 µm/m-°C @Temperature 40.0 - 120 °C |
47.4 µin/in-°F @Temperature 104 - 248 °F |
ASTM E 831 |
| Thermal Conductivity | 0.980 W/m-K | 6.80 BTU-in/hr-ft²-°F | through-plane, ø80*3mm discs; ISO 22007-2 |
| 1.40 W/m-K | 9.72 BTU-in/hr-ft²-°F | through-plane, 10*10*3mm sample; ASTM E 1461-07 | |
| 1.80 W/m-K | 12.5 BTU-in/hr-ft²-°F | in-plane, ø25*0.4mm disc; ASTM E 1461-07 | |
| 2.38 W/m-K | 16.5 BTU-in/hr-ft²-°F | in-plane, ø80*3mm discs; ISO 22007-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | >= 10.0 kV/mm @Thickness 1.00 mm |
>= 254 kV/in @Thickness 0.0394 in |
in oil; ASTM D149 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- PTS Tristar® PC-10FR-(8) 8 MFI Flame Retardant Polycarbonate With Release
- Spartech Centrex® R83/21 ABS Weather Resistant Sheet
- ExxonMobil Mobil Clean 10W-30 Motor Oil
- Dow Corning HS II BASE & 10:1, COLORED CATALYST
- Arlon 0.015" (0.381 mm) Primerless Thermabond® Uncured Silicone (99990A015)
- ATI Wah Chang Hafnium Oxide S Grade, HfO2
- ATI Wah Chang Hafnium Tetrachloride, HfCl4
- Arlon 56224R025 0.025" (0.635 mm) Uncured Silicone Rubber with Fiberglass Substrate
- A. Schulman ComAlloy Hiloy® 656 Nylon 6/6, Carbon/Glass Fiber Reinforced, Flow Enhanced, UL
- Sinotek Materials R20 P Carbon Rod for Dry Battery
Copyright © lookpolymers.com All Rights Reserved