Material Notes:

Product Description: FI0644 is a high molecular weight high density polyethylene copolymer grade specifically designed for blown film applications. Its high molecular weight, broad molecular weight distribution and high density combine successfully to give excellent extrudability with high impact properties.Typical Applications: FI0644 is recommended for blown film extrusion. It can be used for producing heavy duty bags, grocery sacks, shopping bags, refuse bags, liners for multi-wall sacks. The grade is suitable to blend with LLDPE & LDPE and can be used in co-extrusion process.Information provided by SABIC.

Physical Properties	Metric	English	Comments
Density	0.944 g/cc	0.0341 lb/in³	ISO 1183
Thickness	20.0 microns	0.787 mil
Melt Flow	0.18 g/10 min @Load 5.00 kg, Temperature 190 °C	0.18 g/10 min @Load 11.0 lb, Temperature 374 °F	ISO 1133
	5.4 g/10 min @Load 21.6 kg, Temperature 190 °C	5.4 g/10 min @Load 47.6 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	60	60	ISO 868
Film Tensile Strength at Yield, MD	50.0 MPa	7250 psi	ISO 527
Film Tensile Strength at Yield, TD	45.0 MPa	6530 psi	ISO 527
Film Elongation at Break, MD	400 %	400 %	ISO 527
Film Elongation at Break, TD	450 %	450 %	ISO 527
Elmendorf Tear Strength MD	20 g	20 g	ISO 6383-2
Elmendorf Tear Strength TD	40 g	40 g	ISO 6383-2
Elmendorf Tear Strength, MD	1.00 g/micron	25.4 g/mil	ISO 6383-2
Elmendorf Tear Strength, TD	2.00 g/micron	50.8 g/mil	ISO 6383-2
Dart Drop	13.0 g/micron	330 g/mil	F50; ASTM D1709
Dart Drop Test	260 g	0.573 lb	F50; ASTM D1709

Thermal Properties	Metric	English	Comments
Vicat Softening Point	73.0 °C	163 °F	ISO 306
Brittleness Temperature	<= -80.0 °C	<= -112 °F	ASTM D746

Processing Properties	Metric	English	Comments
Melt Temperature	200 - 225 °C	392 - 437 °F
Blow-up Ratio (BUR)	3.0 - 5.0	3.0 - 5.0