Rogers Corporation RT/duroid® 6202PR High Frequency Laminate

Category Polymer
Manufacturer Rogers Corporation
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Rogers Corporation RT/duroid® 6202PR High Frequency Laminate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features:Low loss for excellent high frequency performanceTight dielectric constant and thickness controlExcellent electrical and mechanical propertiesExtremely low thermal coefficient of dielectric constantIn-plane expansion coefficient matched to copperVery low etch shrinkageCopper Cladding - Electrodeposited foil, Resistive foils, RolledLead-free process compatibleTypical Applications:Phase Array AntennasGround Based and Airborne Radar SystemsGlobal Positioning System AntennasPower BackplanesHigh Reliability Complex Multilayer CircuitsCommercial Airline Collision Avoidance SystemsBeam Forming NetworksInformation provided by Rogers Corporation.
Physical Properties Metric English Comments
Density 2.10 g/cc
0.0759 lb/in³
ASTM D792
Moisture Absorption at Equilibrium 0.10 %
0.10 %
D24/23; IPC-TM-650 2.6.2.1
Thickness 127 - 762 microns
5.00 - 30.0 mil
Range of Standard Thicknesses
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 30.0 MPa
4350 psi
X, Y direction; ASTM D638
Elongation at Break 4.9 %
4.9 %
X, Y direction; ASTM D638
Tensile Modulus 1.01 GPa
146 ksi
X, Y direction; ASTM D638
Compressive Modulus 1.035 GPa
150.1 ksi
Z direction; ASTM D638
Thermal Properties Metric English Comments
CTE, linear 15.0 µm/m-°C
8.33 µin/in-°F
X-Direction; 10°C/min; ASTM D3386; IPC-TM-650 2.4.41
15.0 µm/m-°C
8.33 µin/in-°F
Y-Direction; 10°C/min; ASTM D3386; IPC-TM-650 2.4.41
30.0 µm/m-°C
16.7 µin/in-°F
Z-Direction; 10°C/min; ASTM D3386; IPC-TM-650 2.4.41
Specific Heat Capacity 0.930 J/g-°C
0.222 BTU/lb-°F
calculated
Thermal Conductivity 0.680 W/m-K

@Temperature 80.0 °C
4.72 BTU-in/hr-ft²-°F

@Temperature 176 °F
ASTM C518
Decomposition Temperature 500 °C
932 °F
TGA; ASTM D3850
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
Condition A; Z direction; ASTM D257
Surface Resistance 1.00e+15 ohm
1.00e+15 ohm
Condition A; Z direction; ASTM D257
Dielectric Constant 2.86 - 2.94

@Thickness 0.127 mm,
Frequency 1.00e+10 Hz
2.86 - 2.94

@Thickness 0.00500 in,
Frequency 1.00e+10 Hz
Z direction; IPC-TM-650 2.5.5.5
2.86 - 2.94

@Thickness 0.508 mm,
Frequency 1.00e+10 Hz
2.86 - 2.94

@Thickness 0.0200 in,
Frequency 1.00e+10 Hz
Z direction; IPC-TM-650 2.5.5.5
2.94 - 3.02

@Thickness 0.254 mm,
Frequency 1.00e+10 Hz
2.94 - 3.02

@Thickness 0.0100 in,
Frequency 1.00e+10 Hz
Z direction; IPC-TM-650 2.5.5.5
2.96 - 3.04

@Thickness 0.762 mm,
Frequency 1.00e+10 Hz
2.96 - 3.04

@Thickness 0.0300 in,
Frequency 1.00e+10 Hz
Z direction; IPC-TM-650 2.5.5.5
Dissipation Factor 0.0020

@Frequency 1.00e+10 Hz
0.0020

@Frequency 1.00e+10 Hz
Z direction; IPC-TM-650 2.5.5.5
Descriptive Properties Value Comments
Thermal Coefficient of Dielectric Constant 13 ppm/°C
Preliminary; IPC-TM-650 2.5.5.5; 10 GHz; 0°C to 100°C; Z-Direction