Rogers Corporation Poron® 4701-50 Supported Urethane Foam, Firm, PET Supported

Category Polymer , Thermoset , Polyurethane, TS , Thermoset Polyurethane Foam, Unreinforced
Manufacturer Rogers Corporation
Trade Name Poron®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Rogers Corporation Poron® 4701-50 Supported Urethane Foam, Firm, PET Supported.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Firm material used for managing high energy impact with gasketing needs.  Standard available thickness range from 0.012" to 0.500" (0.30 mm to 12.7 mm).Features and Benefits of PORON Products: Excellent compression set resistance which enables durable, long-term performance for gasketing, sealing, and cushioning.Low-outgassing and non-fogging, containing no plasticizers or residual chemicals to contaminate the device. The material will not become brittle and crumble and is non-corrosive to metal.Inherently flame retardant without the use of additives. Many of the materials meet flammability requirements of UL HBF and MVSS 302.Engineered urethane formulations offering a wide modulus range - 2-90 psi @ 25% deflection – for more design versatility requirements.Good chemical resistanceEasy to fabricate, die-cuts cleanly and works with a broad range of adhesivesBroad range of formulas and thicknesses from 0.012" to 0.500" (0.43mm to 12.7mm)Applications:
Physical Properties Metric English Comments
Density 0.481 g/cc
0.0174 lb/in³
ASTM D3574-95 Test A
1.395 g/cc
0.05040 lb/in³
Supporting Material; ASTM D1505
Water Absorption 5.0 %
5.0 %
Immersion; ASTM D570-95
Moisture Absorption at Equilibrium 2.0 %
2.0 %
High Humidity; AMS 3568-95
Thickness 305 microns
12.0 mil
Outgassing - Total Mass Loss 0.060 %

@Temperature 125 °C,
Time 86400 sec
0.060 %

@Temperature 257 °F,
Time 24.0 hour
CVCM; at 7000 Pa; ASTM E595-93
0.43 %

@Temperature 125 °C,
Time 86400 sec
0.43 %

@Temperature 257 °F,
Time 24.0 hour
WVR; at 7000 Pa; ASTM E595-93
0.90 %

@Temperature 125 °C,
Time 86400 sec
0.90 %

@Temperature 257 °F,
Time 24.0 hour
TML; at 7000 Pa; ASTM E595-93
Mechanical Properties Metric English Comments
Hardness, Shore O 55
55
ASTM D2240-97
Tensile Strength 207 MPa
30000 psi
MD, supporting material; ASTM D882
Tensile Strength, Yield 103 MPa
15000 psi
F5, supporting material; ASTM D882
Elongation at Break 150 %
150 %
supporting material; ASTM D882
Tensile Modulus 3.45 GPa
500 ksi
MD, supporting material; ASTM D882
Compressive Yield Strength 0.103 - 0.310 MPa

@Strain 25.0 %
15.0 - 45.0 psi

@Strain 25.0 %
Range, 0.2"/min. strain rate
0.221 MPa

@Strain 25.0 %
32.0 psi

@Strain 25.0 %
Typical value, 0.2"/min. strain rate
Coefficient of Friction, Dynamic 0.40
0.40
A/B, supporting material; ASTM D1894
Compression Set 5.0 %

@Temperature 23.0 °C
5.0 %

@Temperature 73.4 °F
ASTM D1667-90 Test D
10 %

@Temperature 70.0 °C
10 %

@Temperature 158 °F
ASTM D3574-95 Test D
Thermal Properties Metric English Comments
CTE, linear 230 - 310 µm/m-°C
128 - 172 µin/in-°F
Thermal Conductivity 0.0900 W/m-K
0.625 BTU-in/hr-ft²-°F
ASTM C518-98
Maximum Service Temperature, Air 70.0 °C
158 °F
Constant use; SAE J-2236
121 °C
250 °F
Intermittent use; ASTM D746-98
Brittleness Temperature -40.0 °C
-40.0 °F
ASTM D746-98
Shrinkage, MD 1.2 %

@Temperature 150 °C,
Time 2340 sec
1.2 %

@Temperature 302 °F,
Time 0.650 hour
supporting material
Shrinkage, TD 0.00 %

@Temperature 150 °C,
Time 2340 sec
0.00 %

@Temperature 302 °F,
Time 0.650 hour
supporting material
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+12 ohm-cm
2.00e+12 ohm-cm
ASTM D257-99
Dielectric Constant 1.63

@Time 86400 sec
1.63

@Time 24.0 hour
50% RH; ASTM D150
Dielectric Strength 1.97 kV/mm
50.0 kV/in
ASTM D149-97a
Dissipation Factor 0.050
0.050
ASTM D150-98