Qualchem Danamid FGFLX2-30 Polyamide 6, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Qualchem Zrt. |
| Trade Name | Danamid |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Qualchem Danamid FGFLX2-30 Polyamide 6, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Reinforced with glass fiber. Flame retardant, halogen-free (V-2)Information provided by Qualchem Zrt.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.347 g/cc | 0.04866 lb/in³ | DIN 53479 |
| Filler Content | 28 - 32 % | 28 - 32 % |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 90.0 MPa | 13100 psi | 50 mm/min; ISO 527-1,2 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527-1,2 |
| Tensile Modulus | 7.70 GPa | 1120 ksi | ISO 527-1,2 |
| Charpy Impact Unnotched | 2.70 J/cm² @Temperature -30.0 °C |
12.8 ft-lb/in² @Temperature -22.0 °F |
DIN 53453 |
| 3.40 J/cm² @Temperature 23.0 °C |
16.2 ft-lb/in² @Temperature 73.4 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.500 J/cm² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
DIN 53453 |
| 0.700 J/cm² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flammability, UL94 | V-2 @Thickness 4.00 mm |
V-2 @Thickness 0.157 in |
MSZ 10383 |
| Glow Wire Test | 960 °C @Thickness 3.50 mm |
1760 °F @Thickness 0.138 in |
IEC 685-2-1 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | DIN 53482 |
| Comparative Tracking Index | 525 V | 525 V | IEC 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Moisture Content | 2.0 - 2.2 % | 2.0 - 2.2 % | DIN 53714 |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-SEAL® 1270 Conductive Elastomer
- DuPont Performance Polymers Hypalon® 20 Chlorosulfonated Polyethylene Rubber, Mineral Filled Compound (discon
- Haynes 25 alloy, sheet
- A. Schulman LP479-01 High-Density Polyethylene Homopolymer
- A. Schulman INVISION™ VX-5070UI Soft Touch Polyolefin Thermoplastic
- Braskem UTEC® 4040 Ultra High Molecular Weight Polyethylene
- Azoty Tarnow™ TARNOFORM 300 LS POM
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 60 PHR N774 Filler
- SABIC Innovative Plastics LNP LUBRICOMP CX94108 PS (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved