Polyram RamTough RZ222 Polycarbonate, Injection Molding
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamTough RZ222 Polycarbonate, Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polycarbonate for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | DIN 53479 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | |
| Melt Flow | 15 g/10 min @Load 1.20 kg, Temperature 300 °C |
15 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | >= 60.0 MPa | >= 8700 psi | ASTM-D638 |
| Elongation at Break | >= 95 % | >= 95 % | ASTM-D638 |
| Flexural Strength | >= 90.0 MPa | >= 13100 psi | ASTM D790 |
| Flexural Modulus | >= 2.20 GPa | >= 319 ksi | ASTM-D790 |
| Izod Impact, Notched | 7.00 J/cm - NB @Temperature 23.0 °C |
13.1 ft-lb/in - NB @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | >= 130 °C | >= 266 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 120 °C | >= 248 °F | DIN 53461 |
| Vicat Softening Point | 145 °C | 293 °F | ASTM-D1525 |
| Flammability, UL94 | V-2 @Thickness 3.00 mm |
V-2 @Thickness 0.118 in |
|
| Glow Wire Test | 960 °C | 1760 °F |
Users viewing this material also viewed the following:
- Northstar Polymers PAC-004 Curing Agent
- LATI LATAN 13 Medium Viscosity Polyoxymethylene Copolymer (POM) (Unverified Data**)
- Global EPP PA 6C Cast Polyamide 6
- Lehmann & Voss LUVOCOM® 1105/CF/10/GR/10/TF/10-2 PEEK, with carbon fiber, PTFE, lubricant modified
- SABIC Innovative Plastics ULTEM PW1000 PEI (Europe-Africa-Middle East)
- Samsung Cheil Industries Infino® XI-2008F PPS/PPA, Mineral Filled
- Lubrizol ESTANE® 58810 Ether Based Thermoplastic Polyurethane
- Domo 2300K Polypropylene Copolymer
- Arlon R34696R026 0.026" (0.660 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- BASF Isobutylvinylether Stabilized 0.1% DEA
Copyright © lookpolymers.com All Rights Reserved