Polyram RamSter PE300J6 PET, 30% Glass Fiber and Glass Bead Reinforced
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 30% Glass Reinforced |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamSter PE300J6 PET, 30% Glass Fiber and Glass Bead Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% Glass-fiber and glass beads reinforced, high stiffness PET for injection molding applications.Information provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in³ | DIN 53479 |
| Water Absorption | 0.50 % | 0.50 % | DIN 53495 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23° C, 50% RH; DIN 53714 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 280 °C |
10 g/10 min @Load 4.76 lb, Temperature 536 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 110 MPa | 16000 psi | ASTM-D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM-D638 |
| Flexural Strength | 160 MPa | 23200 psi | ASTM D790 |
| Flexural Modulus | 6.00 GPa | 870 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.850 J/cm @Temperature 23.0 °C |
1.59 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| Glow Wire Test | 750 °C | 1380 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | DIN 53482 |
| Dielectric Constant | 3.6 @Frequency 1e+6 Hz |
3.6 @Frequency 1e+6 Hz |
VDE 0303/4 |
| Dielectric Strength | 29.0 kV/mm | 737 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- Nabaltec ACTILOX® B60 AS1 AlO(OH) Boehmite
- Chevron Phillips Dynex™ D605A6 Enhanced LLDPE Blown Film Resin (discontinued **)
- NOVA Chemicals Arcel 310 B 65% PS/35% PE Blue Interpolymer (discontinued **)
- Lehmann & Voss LUVOCOM® 80/TF/18/GY Polyacetal-copolymer, with PTFE
- LG Chemical Lupoy 3010-22 Polycarbonate Resin
- Cossa Polimeri ESTALUX 9202 A Methyl Methacrylate Acrylonitrile Butadiene Styrene
- Crucible Steel JIS SUH11 Martensitic Steel
- DuPont Performance Polymers Delrin® FG100TL NC010 Acetal (POM) (Unverified Data**)
- Spartech EP6430 Filled and Reinforced Copolymer
- Osprey Metals 310S Stainless Steel Powder (Grade 90% - 16)
Copyright © lookpolymers.com All Rights Reserved