Polyram RamShine PAS703 ASA, UV Stabilized
| Category | Polymer , Thermoplastic , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamShine PAS703 ASA, UV Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Is a general purpose injection molding ASA, good chemical resistance, UV stabilization.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0010 - 0.0050 cm/cm | 0.0010 - 0.0050 in/in | ISO 2577 |
| Melt Flow | 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
6.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ISO 527 |
| Elongation at Break | 12.5 % | 12.5 % | ISO 527 |
| Tensile Modulus | 2.28 GPa | 331 ksi | ISO 527 |
| Flexural Strength | 70.0 MPa | 10200 psi | ISO 178 |
| Flexural Modulus | 3.00 GPa | 435 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 101 °C | 214 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 GF 50 LS PA6, 50% glass fibre, light stability
- Polymax® Maxelast® P3857CT TPE, PP Overmold or Standalone use
- Parker Chomerics CHO-BOND 360-208 Conductive Epoxy
- Polymer Resources PPX-GP3-WR Modified-PPO, Wear Resistant
- Reade Advanced Materials Diopside Powder (CaMg(CO3)2 and CaMg(SiO3)2)
- H.C. Starck Amperit® 518.088 Agglomerated, Sintered Tungsten Carbide-Cobalt 88-12 (WC-CO)
- Lucite International Colacryl ® D1-120 Acrylic Dental Resin
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 40 PHR Carbon Black, N-550 (FEF)
- M. Holland Company MAGMA® LM311-D LLDPE (discontinued **)
- ATI Allegheny Ludlum Martensitic Stainless Steel Type 410, Annealed
Copyright © lookpolymers.com All Rights Reserved