Zotefoams ZOTEK® F OSU Flexible PVDF Foam

Category	Polymer , Thermoplastic , Fluoropolymer , PVDF
Manufacturer	Zotefoams
Trade Name	ZOTEK®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Zotefoams ZOTEK® F OSU Flexible PVDF Foam.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Zotek® F OSU is a closed cell foam made from Arkema Kynar® PVDF manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outstanding physical attributes.This grade is ideal for soft trim in combination with leathers, textiles and decorative laminates.Information provided by Zotefoams

Physical Properties	Metric	English	Comments
Density	0.0330 g/cc	0.00119 lb/in³	ISO 845
Water Absorption	0.060 %	0.060 %	ISO 2896
	2.2 %	2.2 %	ASTM 1056

Mechanical Properties	Metric	English	Comments
Tensile Strength	0.245 MPa	35.5 psi	ISO 1798
Elongation at Break	88 %	88 %
Compressive Yield Strength	0.0600 MPa @Strain 25.0 %	8.70 psi @Strain 25.0 %	ISO 7214
Compression Set	17 % @Time 79200 sec, Strain 50.0 %	17 % @Time 22.0 hour, Strain 50.0 %	0.5 hr recovery; ISO 7214

Thermal Properties	Metric	English	Comments
Thermal Conductivity	0.0330 W/m-K	0.229 BTU-in/hr-ft²-°F	mean temp of 0°C; ISO 8301
	0.0380 W/m-K	0.264 BTU-in/hr-ft²-°F	mean temp of 40°C; DIN 52 612
	0.0460 W/m-K	0.319 BTU-in/hr-ft²-°F	mean temp of 80°C; ASTM C 518
Maximum Service Temperature, Air	110 °C	230 °F

Descriptive Properties	Value	Comments
Flammability	Heat Release: FAR/CS 25.853, 2 min total	39.8 kWmin/m<sup>2</sup> at 25 mm
	Heat Release: FAR/CS 25.853, Peak	49.1 kW/m<sup>2</sup> at 25 mm
	Radiant Heat Panel: FAR 25.856	Pass at 3, 13, and 25 mm
	Smoke Density: ABD0031	Pass at 3 and 13 mm
	Smoke Density: FAR/CS 25.853	Pass at 3 and 13 mm
	Toxic Gas Emission: ABD0031	Pass at 3 and 13 mm
	Vertical Bunsen Burner: FAR/CS 25.853	Pass at 3 and 13 mm