Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), Glass Fiber Filled, Flame Retardant |
Manufacturer | Toyobo |
Trade Name | VYLOPET® |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | Toyobo Vylopet® EMC130-04 Glass Reinforced Polyester, Easy Molding Grade.pdf |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.65 g/cc | 0.0596 lb/in³ | ASTM D792 |
Water Absorption | 0.050 % | 0.050 % | ASTM D570 |
Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | |
Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Hardness, Rockwell M | 93 | 93 | ASTM D785 |
Tensile Strength, Ultimate | 132 MPa | 19100 psi | ASTM D638 |
Elongation at Break | 1.9 % | 1.9 % | ASTM D638 |
Flexural Yield Strength | 177 MPa | 25700 psi | ASTM D790 |
Flexural Modulus | 9.80 GPa | 1420 ksi | ASTM D790 |
Compressive Yield Strength | 98.0 MPa | 14200 psi | ASTM D695 |
Izod Impact, Notched | 1.20 J/cm | 2.25 ft-lb/in | ASTM D256 |
Taber Abrasion, mg/1000 Cycles | 25 | 25 | ASTM D1044 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
Melting Point | 255 °C | 491 °F | DSC |
Deflection Temperature at 0.46 MPa (66 psi) | 235 °C | 455 °F | ASTM D648 |
Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ASTM D648 |
UL RTI, Electrical | 130 °C | 266 °F | UL-746B |
Flammability, UL94 | V-0 @Thickness 0.7937 mm |
V-0 @Thickness 0.03125 in |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
Dielectric Strength | 24.0 kV/mm @Thickness 2.00 mm |
610 kV/in @Thickness 0.0787 in |
ASTM D149 |
Arc Resistance | 83 sec | 83 sec | ASTM D495 |
Comparative Tracking Index | 220 V | 220 V | IEC test |