- Polyram Polytron P30B07 Polypropylene, 30% Long Glass Fibers, UV Stabilized
Polyram Polytron P30B07 Polypropylene, 30% Long Glass Fibers, UV Stabilized
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler |
| Manufacturer | Polyram |
| Trade Name | Polytron |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram Polytron P30B07 Polypropylene, 30% Long Glass Fibers, UV Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A chemically coupled 30% long glass fibers reinforced black polypropylene, heat stabilized, UV stabilized for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0017 cm/cm | 0.0017 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 110 MPa | 16000 psi | ISO 527 |
| Elongation at Break | 2.6 % | 2.6 % | ISO 527 |
| Tensile Modulus | 7.75 GPa | 1120 ksi | ISO 527 |
| Flexural Strength | 160 MPa | 23200 psi | ISO 178 |
| Flexural Modulus | 6.45 GPa | 935 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 18.0 kJ/m² | 8.57 ft-lb/in² | ISO 180 |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 1.80 J/cm² | 8.57 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 167 °C | 333 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| Flame Spread | 30 mm/min | 1.2 in/min | FMVSS302 |
| Glow Wire Test | 750 °C | 1380 °F | GWFI; IEC 60695 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 144 PC (Asia Pacific)
- LG Chemical NBR 6230 High Acrylonitrile Polymer
- Goodfellow Cobalt 90/Aluminum 10 Alloy
- Cotronics Resbond™ 907 High Temperature Ceramic Adhesive, Industrial Strength
- Epoxy Technology EPO-TEK® ED1021 Epoxy
- Chosun Refractories SAL85N Special Alumina brick
- ConocoPhillips EP Conolith® Grease NLGI NO. 000
- BNZ Materials BNZ-23A Insulating Firebrick
- ACC EP RSP EPI Engineered Polymers Silicone Polyurea
Copyright © lookpolymers.com All Rights Reserved