Polymer Resources PPX/NY G30 Modified PPO, 30% Glass Reinforced PPX/Nylon 6,6 Alloy  (Unverified Data**)&l

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, 30% Glass Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources PPX/NY G30 Modified PPO, 30% Glass Reinforced PPX/Nylon 6,6 Alloy  (Unverified Data**)&l.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Density 1.33 g/cc
0.0480 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
ASTM D955
Melt Flow 1.0 - 4.0 g/10 min
1.0 - 4.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 148 MPa
21500 psi
ASTM D638
Tensile Strength, Yield 148 MPa
21500 psi
ASTM D638
Flexural Strength 221 MPa
32000 psi
ASTM D790
Flexural Modulus 8.14 GPa
1180 ksi
ASTM D790
Izod Impact, Notched 0.481 J/cm
0.900 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 227 °C
440 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 232 °C
450 °F
ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 268 - 302 °C
515 - 575 °F
Middle Barrel Temperature 274 - 302 °C
525 - 575 °F
Front Barrel Temperature 279 - 302 °C
535 - 575 °F
Melt Temperature 279 - 304 °C
535 - 580 °F
Mold Temperature 79.4 - 121 °C
175 - 250 °F
Drying Temperature 93.3 - 107 °C
200 - 225 °F
Dry Time 3 - 5 hour
3 - 5 hour