Polymer Resources PPX/NY G20 Modified PPO, 20% Glass Reinforced PPX/Nylon 6,6 Alloy (Unverified Data**)&l

Category	Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, 20% Glass Filled
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polymer Resources PPX/NY G20 Modified PPO, 20% Glass Reinforced PPX/Nylon 6,6 Alloy (Unverified Data**)&l.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.

Physical Properties	Metric	English	Comments
Density	1.25 g/cc	0.0452 lb/in³	ASTM D792
Linear Mold Shrinkage	0.0040 - 0.0070 cm/cm	0.0040 - 0.0070 in/in	ASTM D955
Melt Flow	1.0 - 4.0 g/10 min	1.0 - 4.0 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	114 MPa	16500 psi	ASTM D638
Tensile Strength, Yield	114 MPa	16500 psi	ASTM D638
Flexural Strength	169 MPa	24500 psi	ASTM D790
Flexural Modulus	5.38 GPa	780 ksi	ASTM D790
Izod Impact, Notched	0.481 J/cm	0.900 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	210 °C	410 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	221 °C	430 °F	ASTM D648

Processing Properties	Metric	English
Rear Barrel Temperature	268 - 302 °C	515 - 575 °F
Middle Barrel Temperature	274 - 302 °C	525 - 575 °F
Front Barrel Temperature	279 - 302 °C	535 - 575 °F
Melt Temperature	279 - 302 °C	535 - 575 °F
Mold Temperature	79.4 - 121 °C	175 - 250 °F
Drying Temperature	93.3 - 107 °C	200 - 225 °F
Dry Time	3 - 5 hour	3 - 5 hour

Users viewing this material also viewed the following: