Polymer Resources AC-G10 Acetal Copolymer, 10% Glass Reinforced
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 10% Glass Fiber Reinforced |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources AC-G10 Acetal Copolymer, 10% Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.49 g/cc | 1.49 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.010 - 0.015 cm/cm | 0.010 - 0.015 in/in | ASTM D955 |
| Melt Flow | 1.0 - 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.0 - 4.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 48.3 MPa | 7000 psi | ASTM D638 |
| Tensile Strength, Yield | 48.3 MPa | 7000 psi | ASTM D638 |
| Flexural Strength | 75.8 MPa | 11000 psi | ASTM D790 |
| Flexural Modulus | 2.62 GPa | 380 ksi | ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm @Temperature 22.8 °C |
0.500 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 310 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 350 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0626 in |
|
| HB @Thickness 3.17 mm |
HB @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 177 - 188 °C | 350 - 370 °F | |
| Middle Barrel Temperature | 182 - 193 °C | 360 - 380 °F | |
| Front Barrel Temperature | 188 - 199 °C | 370 - 390 °F | |
| Melt Temperature | 199 - 213 °C | 390 - 415 °F | |
| Mold Temperature | 82.2 - 107 °C | 180 - 225 °F | |
| Drying Temperature | 79.4 - 85.0 °C | 175 - 185 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Vent | 0.0005 |
Users viewing this material also viewed the following:
- Plaskolite Optix® Acrylic Sheet
- Multibase Multi-Flex® A 6221 TPE Thermoplastic Elastomer
- Latrobe Knocorâ„¢ Hot Work Tool Steel
- Borealis Borsoft™ SD233CF High Impact Polypropylene Random Heterophasic Copolymer for Cast Film
- Master Bond Mastersil 701 One Component, Room Temperature Curing Silicone Elastomer
- Master Bond MB600S Aqueous Based Sodium Silicate System for EMI/RFI Shielding
- CTC X-PRO PP 100 P1015 Polypropylene Homopolymer
- AK Steel 305 Austenitic Stainless steel
- Asahi Kasei Thermofil N-40MF-0350 40% Mineral Filled, Heat Stabilized
- 3M Scotch® 311 Box Sealing Tape
Copyright © lookpolymers.com All Rights Reserved