Polykemi AB POLYform POM C M90 K5 Polyoxymethylene, Mineral Reinforced
| Category | Polymer , Thermoplastic |
| Manufacturer | Polykemi AB |
| Trade Name | POLYform |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYform POM C M90 K5 Polyoxymethylene, Mineral Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.018 - 0.020 cm/cm | 0.018 - 0.020 in/in | With Flow; ISO 2577 |
| 0.018 - 0.020 cm/cm | 0.018 - 0.020 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 62.0 MPa | <= 8990 psi | ISO/R527 |
| Elongation at Yield | 8.0 % | 8.0 % | ISO/R527 |
| Flexural Strength | <= 93.0 MPa | <= 13500 psi | ISO 178 |
| Flexural Modulus | 2.70 GPa @Temperature 23.0 °C |
392 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 0.500 J/cm² @Temperature -20.0 °C |
2.38 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| 0.700 J/cm² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 150 °C @Load 5.001 kg |
302 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
Users viewing this material also viewed the following:
- Polimeri Europa Flexirene® FG 23 U Butene Copolymer Linear Low Density Polyethylene
- Multibase Multi-Flex® TPO D-6206
- Mitsui Fybrel® E 400 Polyolefin Synthetic Pulp, Wet Processes (discontinued **)
- Karina 901D10/146-B-AT White PVC Compound
- Hardwire 3SX-21.5-12 High Density Composite
- Loctite® 3900 Acrylic Aerosol Coating
- Chosun Refractories CRAG-L44 Shroud Nozzle
- BASF Ultramid® 8233G HS 33% Glass Filled PA6 (Conditioned)
- BASF Capron® 8351 Impact Modified Nylon 6 (Conditioned) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved