PolyOne Therma-Tech™ SFC-5000 TC Polyphenylene Sulfide (PPS)  (discontinued **)

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Therma-Tech™ SFC-5000 TC Polyphenylene Sulfide (PPS)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Therma-Tech™ Thermal Management Compounds have been engineered to combine the heat transfer and cooling capabilities of metals with the design freedom, weight reduction and cost advantages of thermoplastics. These materials provide the benefits of proprietary conductive additive technologies and the performance of select engineering thermoplastic resins. Therma-Tech compounds have been shown to improve thermal conductivity up to 100-times that of conventional plastics and can be used in a wide range of thermal management applications.Description/Features:PPS (Polyphenylenesulfide)Thermally ConductiveElectrically ConductiveApplications: EnclosuresHeat SinksMotor componentsProcessing Method: Injection MoldingInformation provided by PolyOne Corporation
Physical Properties Metric English Comments
Specific Gravity 1.70 g/cc
1.70 g/cc
ASTM D792
Water Absorption 0.030 %

@Thickness 3.17 mm
0.030 %

@Thickness 0.125 in
24 hr. Immersion; ASTM D570
Linear Mold Shrinkage 0.0030 - 0.0050 cm/cm
0.0030 - 0.0050 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Yield 62.1 MPa
9000 psi
Type 1 - Rigids, Yield, 0.2 in/min; ASTM D638
Elongation at Break 0.30 %
0.30 %
Type 1 - Rigids, 0.2 in/min; ASTM D638
Tensile Modulus 22.1 GPa
3200 ksi
Type 1 - Rigids, 0.2 in/min; ASTM D638
Flexural Strength 100 MPa
14500 psi
ASTM D790
Flexural Modulus 19.3 GPa
2800 ksi
ASTM D790
Izod Impact, Notched 0.267 J/cm

@Thickness 6.35 mm,
Temperature 23.0 °C
0.500 ft-lb/in

@Thickness 0.250 in,
Temperature 73.4 °F
Method A, Injection Molded; ASTM D256
Thermal Properties Metric English Comments
Thermal Conductivity 1.00 - 2.00 W/m-K
6.94 - 13.9 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 0.46 MPa (66 psi) 277 °C
530 °F
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 260 °C
500 °F
Unannealed; ASTM D648
Electrical Properties Metric English Comments
Volume Resistivity 100 - 1000 ohm-cm
100 - 1000 ohm-cm
ASTM D257
Surface Resistivity per Square 10 - 100 ohm
10 - 100 ohm
ASTM D257
Processing Properties Metric English Comments
Melt Temperature 316 - 329 °C
600 - 625 °F
Molding
Mold Temperature 121 - 149 °C
250 - 300 °F