| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Glass Bead Filled |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ AS-10GB/02S Acrylonitrile Butadiene Styrene (ABS), Glass Bead Filled
(discontinued **)<.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Bead FilledSilicone LubricatedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.11 g/cc | 1.11 g/cc | ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 36.5 MPa | 5300 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 2.69 GPa | 390 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 37.2 MPa | 5400 psi | ASTM D790 |
| Flexural Modulus | 2.69 GPa | 390 ksi | ASTM D790 |
| Izod Impact, Notched | 0.667 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.25 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 227 - 243 °C | 440 - 470 °F | Molding |
| Mold Temperature | >= 65.6 °C | >= 150 °F | |
| Drying Temperature | 65.6 °C | 150 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 2520 XU Black Polypropylene
- Mitsui Fybrel® E 780 Polyolefin Synthetic Pulp, Dry Processes (discontinued **)
- PolyOne Edgetek® SF-40GF-25MN1/000 PPS (Polyphenylene Sulfide), 40% Glass Fiber and 25% Mineral Filled (disco
- Meehanite HE Heat Resisting Cast Iron
- Michelman® Michem® Lube 190 Anionic polyethylene wax emulsion
- Mid-Mountain Materials HYTEX® 5000 High Carbon Industrial Textile (PAN)
- Samsung Cheil Industries Infino® TK-2046H PCT, Glass Filled
- Covestro Makrolon® 2800 Polycarbonate
- Ashley Polymers Ashlene® 527LDW Nylon 66
- A. Schulman ComAlloy Hiloy® 616 Nylon 6, Mineral Reinforced
Copyright © lookpolymers.com All Rights Reserved