Zircar Refractory Composites RS-B ALUMINA-SILICA MOLDABLE

Category	Ceramic , Oxide , Aluminum Oxide , Silicon Oxide
Manufacturer	Zircar Refractory Composites, Inc.
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Zircar Refractory Composites RS-B ALUMINA-SILICA MOLDABLE.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

ZIRCAR Alumina-Silica Insulating Blanket Type RS-B Moldable is composed of long, high strength ceramic fibers, with an inorganic alumina binder/rigidizing agent. It is a wet blanket that is shipped rolled up and sealed in a plastic bag to preserve its moldability.Information provided by ZIRCAR Refractory Composites, Inc. (ZRCI)

Physical Properties	Metric	English	Comments
Density	0.300 g/cc	0.0108 lb/in³

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	1.20 MPa	174 psi
Compressive Yield Strength	0.0700 MPa	10.2 psi	at 10% Compression

Thermal Properties	Metric	English	Comments
Thermal Conductivity	0.0700 W/m-K @Temperature 200 °C	0.486 BTU-in/hr-ft²-°F @Temperature 392 °F	parallel to thickness; ASTM C177
	0.100 W/m-K @Temperature 500 °C	0.694 BTU-in/hr-ft²-°F @Temperature 932 °F	parallel to thickness; ASTM C177
	0.160 W/m-K @Temperature 800 °C	1.11 BTU-in/hr-ft²-°F @Temperature 1470 °F	parallel to thickness; ASTM C177
Maximum Service Temperature, Air	900 °C	1650 °F
Shrinkage	0.000 % @Temperature 75.0 °C	0.000 % @Temperature 167 °F	Drying perpendicular to thickness
	3.00 % @Temperature 75.0 °C	3.00 % @Temperature 167 °F	Drying parallel to thickness
	2.00 % @Temperature 800 °C, Time 86400 sec	2.00 % @Temperature 1470 °F, Time 24.0 hour	perpendicular to thickness

Component Elements Properties	Metric	English
Al2O3	33 %	33 %
Other	26 %	26 %
SiO2	41 %	41 %

Descriptive Properties	Value	Comments
Color	White