- Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled
- PolyOne Stat-Tech™ AS-15GF/000 SD ABS - 15% Glass Fiber Reinforced - Antistatic Protection (discontinued **)&
PolyOne Stat-Tech™ AS-15GF/000 SD ABS - 15% Glass Fiber Reinforced - Antistatic Protection (discontinued **)&
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Stat-Tech™ AS-15GF/000 SD ABS - 15% Glass Fiber Reinforced - Antistatic Protection
(discontinued **)&.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by PolyOne.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | 24 hrs. ASTM D570 |
| Water Absorption at Saturation | 0.80 % | 0.80 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0020 cm/cm @Thickness 3.17 mm |
0.0020 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
| Elongation at Break | 2.0 - 4.0 % | 2.0 - 4.0 % | ASTM D638 |
| Tensile Modulus | 4.80 GPa | 696 ksi | ASTM D638 |
| Izod Impact, Notched | 0.690 J/cm @Thickness 6.35 mm |
1.29 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+9 - 1.00e+13 ohm | 1.00e+9 - 1.00e+13 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 221 - 243 °C | 430 - 469 °F | Stock |
| Mold Temperature | 27.0 - 54.0 °C | 80.6 - 129 °F | |
| Drying Temperature | 82.0 °C | 180 °F |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 GF 20 LS PA6, 20% glass beads, light stability
- Polymer Resources PPX-MF-FR1 Modified-PPO, V-0 Flame Retardant, Mineral Reinforced
- H.C. Starck Amperit® 515.2 Sintered Tungsten Carbide - Cobalt (WC-Co) 88-12
- Silikony Polskie Polastosil M-99 Silicone Rubber
- ExxonMobil 680 Mobil DTE FM Series
- A. Schulman POLYBATCH™ Yellow 2200 Concentrate Based In Polyethylene
- Diamond Polymers ABS 4107 Heat Resistant Grade
- Clariant PA621G30 Nylon 612, 30% Glass Fiber, Impact Modified
- Aremco Aremco-Bond™ 568 High Performance Epoxide
- PolyOne Lubri-Tech™ RA-15GF/13T Polyethersulfone, Glass Filled, PTFE Lubricated (discontinued **)
Copyright © lookpolymers.com All Rights Reserved